Molten aluminum slag remover and preparation method and application thereof

A technology for slag agent and molten aluminum, applied in the field of molten aluminum slag remover and its preparation, can solve problems such as poor separation effect, and achieve the effect of strong separation effect and avoidance of pores

Inactive Publication Date: 2021-04-30
GUANGDONG HONGBANG ALUMINUM METAL IND CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, inert gas is generally introduced into the molten aluminum to bring out impurities, and the separation effect of this method is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A liquid aluminum slag remover, comprising the following raw materials in parts by weight: 30 parts of sodium chloride, 20 parts of potassium chloride, 8 parts of sodium fluorosilicate, and 6 parts of fluorite.

[0018] The preparation method of the aluminum liquid deslagging agent specifically comprises the following steps;

[0019] Weigh the proportioned raw materials according to their weight, and preliminarily dry the weighed raw materials to make their moisture content < 2%, respectively pulverize the preliminarily dried raw materials, and use the pulverizer in this field to carry out Preliminary crushing, the crushed raw materials are passed through a 20-mesh sieve, and fully mixed to obtain material A;

[0020] The material A is dried twice to make its moisture content <0.2%, and the material B is obtained, and the material B is subjected to secondary crushing, and the crushed material B is passed through a 50-mesh sieve to obtain the material C.

[0021] The in...

Embodiment 2

[0026] A liquid aluminum slag remover comprises the following raw materials in parts by weight: 35 parts of sodium chloride, 25 parts of potassium chloride, 12 parts of sodium fluorosilicate and 7 parts of fluorite.

[0027] The preparation method of the aluminum liquid deslagging agent specifically comprises the following steps;

[0028] Weigh the proportioned raw materials according to their weight, and preliminarily dry the weighed raw materials to make their moisture content < 2%, respectively pulverize the preliminarily dried raw materials, and use the pulverizer in this field to carry out Preliminary crushing, the crushed raw materials are passed through a 20-mesh sieve, and fully mixed to obtain material A;

[0029] The material A is dried twice to make its moisture content <0.2%, and the material B is obtained, and the material B is subjected to secondary crushing, and the crushed material B is passed through a 50-mesh sieve to obtain the material C.

[0030] The init...

Embodiment 3

[0035] A liquid aluminum slag remover comprises the following raw materials in parts by weight: 40 parts of sodium chloride, 30 parts of potassium chloride, 16 parts of sodium fluorosilicate and 8 parts of fluorite.

[0036] The preparation method of the aluminum liquid deslagging agent specifically comprises the following steps;

[0037] Weigh the proportioned raw materials according to their weight, and preliminarily dry the weighed raw materials to make their moisture content < 2%, respectively pulverize the preliminarily dried raw materials, and use the pulverizer in this field to carry out Preliminary crushing, the crushed raw materials are passed through a 20-mesh sieve, and fully mixed to obtain material A;

[0038] The material A is dried twice to make its moisture content <0.2%, and the material B is obtained, and the material B is subjected to secondary crushing, and the crushed material B is passed through a 50-mesh sieve to obtain the material C.

[0039] The init...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a molten aluminum slag remover and a preparation method and application thereof, and belongs to the technical field of molten aluminum refining. The slag remover comprises the following raw materials in parts by weight: 30-50 parts of sodium chloride, 20-40 parts of potassium chloride, 10-20 parts of sodium fluosilicate and 4-8 parts of fluorite. The preparation method comprises the following steps of: preparing 35 parts of sodium chloride, 25 parts of potassium chloride, 12 parts of sodium fluosilicate and 7 parts of fluorite into the slag remover; mixing the slag remover and inputting into molten aluminum in a furnace for stirring; inputting gas D into the molten aluminum while stirring; and finally, filtering out dross to complete refined aluminum purification. The infiltration effect of the molten aluminum is guaranteed by using sodium chloride and potassium chloride, and separation of hydrogen in the molten aluminum is guaranteed by using potassium chloride; and as the partial pressures of the gas D and hydrogen in the molten aluminum are different, hydrogen generated in the molten aluminum enters bubbles and then escapes from the liquid surface, so that hydrogen generated in the molten aluminum can be removed, generation of pores is avoided, and the separation effect is strong.

Description

technical field [0001] The invention relates to the technical field of aluminum liquid refining, in particular to a liquid aluminum slag remover and its preparation method and application. Background technique [0002] When aluminum alloy is smelted, due to the reaction between aluminum and water or oxygen in the air, harmful gases or solid particles will be produced. Such aluminum liquid will produce a series of quality problems such as pores, knives, and slag during deep processing and casting. Therefore, the aluminum liquid must be refined and purified. At present, inert gas is generally introduced into molten aluminum to bring out impurities, and the separation effect of this method is poor. Contents of the invention [0003] The purpose of the present invention is to provide a liquid aluminum slag remover and its preparation method and application, to solve the problems raised in the above-mentioned background technology. [0004] To achieve the above object, the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B21/06C22B9/10C22B9/05C22C1/06
CPCC22B21/062C22B21/064C22B9/106C22B9/05C22C1/06
Inventor 闫俊
Owner GUANGDONG HONGBANG ALUMINUM METAL IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com