Composite material in-mold coating process

A technology of composite materials and inner coating, applied in coating and other directions, can solve problems such as difficult operation

Active Publication Date: 2021-07-06
中机精密成形产业技术研究院(安徽)股份有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a composite material in-mold coating process to solve the technical problem in the prior art that it is difficult to directly press the cured coating on the surface of the workpiece for complex-shaped workpieces

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite material in-mold coating process
  • Composite material in-mold coating process
  • Composite material in-mold coating process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0043] Next, the technical solutions in the embodiments of the present invention will be apparent from the embodiment of the present invention, and it is clearly described, and it is understood that the described embodiments are merely embodiments of the present invention, not all of the embodiments. Based on the embodiments of the present invention, there are all other embodiments obtained without making creative labor without making creative labor premises.

[0044] Such as figure 1 As shown, a composite molded coating process is characterized in that the following steps are included.

[0045] Step 100. After the mold is prepared, the release agent is sprayed into the surface of the mold through the peripheral device;

[0046] Step 200, after mixing the coating and the curing agent, spray the surface of the mold through the peripheral device according to the predetermined track, and form a solidified lattice layer on the surface of the mold by controlling the curing condition;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a composite material in-mold coating process. The composite material in-mold coating process comprises the following steps that step 100, after a mold is pretreated, a release agent is evenly sprayed to the surface of the mold through an external device; step 200, a coating and a curing agent are mixed according to a proportion, the coating and the curing agent are sprayed on the surface of the mold through the external device according to a preset track, and a cured gel coat layer is formed on the surface of the mold by controlling curing conditions; step 300, a prefabricated part which is made of the same material as the coating is put into a mold, and compression molding is carried out by controlling molding conditions; and step 400, demolding is carried out, and a formed workpiece is taken out and is subjected to post-treatment. The composite material in-mold coating process is adopted, the gel coat is evenly sprayed on the surface of the mold, after the coating is cured, raw materials are put into the mold to be cured and formed, then a product can be taken out to obtain a colored product, the surface of the workpiece is covered with the gel coat coating while the workpiece is formed, the formed workpiece covered with the gel coat layer is obtained at a time, the original paint spraying procedure is simplified, and the pressing difficulty is reduced.

Description

Technical field [0001] The present invention relates to the field of composite surface treatment techniques, and more particularly to a composite molded coating process. Background technique [0002] Composites are widely used in various fields due to their high materials, high impact strength, high temperature difference, anti-aging, anti-corrosion, lightning, static electricity and high compatibility with various materials. In the surface of the composite lacquer, the color unevenness of the surface of the article can eliminate the disadvantage of the surface of the article, supplemented with insufficient molding and adjustment of surface gloss. [0003] At present, the existing composite product spraying method is similar to the painting of metal products. The first is cleaning, handling the surface of the article, the surface of the article, ensures the finish, and then uses a dedicated putty according to the surface conditions, followed by spraying. However, this spray metho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C51/00B29C51/26B29C51/30B29C51/46B29C33/56B29C33/58
CPCB29C51/00B29C51/26B29C51/30B29C51/46B29C33/56B29C33/58
Inventor 王小刚郭平安边翊金康孙奋丽何增云
Owner 中机精密成形产业技术研究院(安徽)股份有限公司
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com