Hydrophilic antibacterial non-woven fabric preparation process
A preparation process and antibacterial technology, which is applied in the field of preparation technology of hydrophilic antibacterial non-woven fabrics, can solve the problems of not being suitable for household and wearing use, poor antibacterial effect of polyester layer, poor hydrophilic effect, etc., and achieve excellent environmental protection properties, long-lasting antibacterial effect, excellent hydrophilic effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0026] A preparation process of hydrophilic antibacterial non-woven fabric, comprising the following steps,
[0027] S1) adopt dipping method to carry out hydrophilic finishing to silver series polyester antibacterial staple fiber, hydrophilic finishing process is: use polyester finishing agent T200, its consumption is 3% (o.w.f), bath ratio is 1:10, and dipping time is 20min, The dipping temperature is 40±2°C, dehydrating the silver-based polyester antibacterial staple fibers after hydrophilic finishing, drying at 105°C, opening, and carding to obtain the polyester layer;
[0028] S2) Opening and combing the natural fibers to obtain the lower layer of cotton, and spraying an antibacterial finishing agent on the lower layer of cotton, the amount of antibacterial finishing is 20g / L, and drying at 180°C;
[0029] S3) hot-rolling the polyester layer and the lower layer of cotton to obtain a composite layer;
[0030] S4) Evenly spray softening treatment liquid on the upper surfac...
Embodiment 2
[0033] A preparation process of hydrophilic antibacterial non-woven fabric, comprising the following steps,
[0034] S1) adopt dipping method to carry out hydrophilic finishing to silver series polyester antibacterial staple fiber, hydrophilic finishing process is: use polyester finishing agent T200, its consumption is 8% (o.w.f), bath ratio is 1:10, dipping time is 20min, The dipping temperature is 40±2°C, dehydrating the silver-based polyester antibacterial staple fibers after hydrophilic finishing, drying at 105°C, opening, and carding to obtain the polyester layer;
[0035] S2) Opening and combing the natural fibers to obtain the lower layer of cotton, spraying an antibacterial finishing agent on the lower layer of cotton, the amount of antibacterial finishing is 40g / L, and drying at 160°C;
[0036] S3) hot-rolling the polyester layer and the lower layer of cotton to obtain a composite layer;
[0037] S4) Evenly spray softening treatment liquid on the upper surface of the...
Embodiment 3
[0040] A preparation process of hydrophilic antibacterial non-woven fabric, comprising the following steps,
[0041] S1) adopt dipping method to carry out hydrophilic finishing to silver series polyester antibacterial staple fiber, hydrophilic finishing process is: use polyester finishing agent T200B, its consumption is 5% (o.w.f), bath ratio is 1:10, and dipping time is 20min, The dipping temperature is 40±2°C, dehydrating the silver-based polyester antibacterial staple fibers after hydrophilic finishing, drying at 105°C, opening, and carding to obtain the polyester layer;
[0042] S2) Opening and combing the natural fibers to obtain the lower layer of cotton, spraying an antibacterial finishing agent on the lower layer of cotton, the amount of antibacterial finishing is 50g / L, and drying at 160°C;
[0043] S3) hot-rolling the polyester layer and the lower layer of cotton to obtain a composite layer;
[0044] S4) Evenly spray softening treatment liquid on the upper surface o...