A non-iron finishing process for shirts

A technology for non-iron finishing and shirting, which is applied to fiber processing, plant fibers, fibers that affect crease behavior, etc., can solve the problems of yellowing of cotton shirts, improve whiteness, improve non-iron washability, and improve non-iron performance effect

Active Publication Date: 2022-07-15
浙江东廷服饰有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to improve the yellowing problem of cotton shirts after chitosan finishing, the application provides a non-ironing finishing process for shirts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0045] The preparation process of the chitosan finishing liquid is as follows: 1.2 parts of chitosan, 6 parts of citric acid, 0.05 parts of sodium hypophosphite, 0.12 parts of emulsifier OP-10 and 100 parts of water are mixed and stirred uniformly.

preparation example 2

[0047] The preparation process of the chitosan finishing solution is as follows: 1.5 parts of chitosan, 8 parts of citric acid, 0.08 parts of sodium hypophosphite, 0.15 parts of emulsifier OP-10 and 120 parts of water are mixed and stirred uniformly.

preparation example 3

[0049] The preparation process of the chitosan finishing liquid is as follows: 1.3 parts of chitosan, 7 parts of citric acid, 0.06 parts of sodium hypophosphite, 0.14 parts of emulsifier OP-10 and 110 parts of water are mixed and stirred uniformly.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present application relates to the technical field of garment finishing, and specifically discloses a non-iron finishing process for shirts. The non-iron finishing process of shirts includes the following steps: S1 pre-cleaning; S2 chitosan finishing; S3 epoxy resin finishing: immerse the cotton shirts finished with S2 chitosan into the epoxy resin finishing solution, one dipping and one rolling, and the immersion temperature is 60°C ‑80℃, dipping time 20‑30min, residual ratio 90%, after taking out, pre-bake at 90‑100℃ for 4‑6min, then bake at 170‑190℃ for 90‑120s, then wash with water and dry; S4 Pressing and shaping: Pressing and shaping each part of the cotton shirt finished with S3 epoxy resin, the pressing temperature is 130-150°C, to obtain a non-iron shirt. The present application adopts the method of finishing with chitosan first and then finishing with epoxy resin, so as to improve the whiteness of cotton shirts and the resistance to ironing and washing.

Description

technical field [0001] The present application relates to the field of garment finishing, more specifically, it relates to a non-iron finishing process for shirts. Background technique [0002] Cotton shirts have the advantages of soft hand feel, good moisture absorption and air permeability, etc., but they are easy to wrinkle and need to be ironed after washing, which is troublesome. In order to avoid the trouble of ironing, iron-free shirts are currently very popular in the market. A non-iron shirt is a 100% cotton textured shirt that can be restored flat after ordinary washing without ironing or a little ironing. The non-iron finishing of shirts mostly uses the initial shrinkage of amide and formaldehyde. Although a higher non-iron grade can be obtained, it does not conform to the current environmental protection concept. [0003] At present, many kinds of formaldehyde-free finishing agents have been developed, such as: chitosan finishing agent, silicone finishing agent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/03D06M15/55D06M11/79D06M13/207D06M11/70D06M13/144D06M101/06
CPCD06M15/03D06M15/55D06M11/79D06M13/207D06M11/70D06M13/144D06M2200/20D06M2101/06
Inventor 王光强刘正林
Owner 浙江东廷服饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com