Lightweight environment-friendly brick manufactured from construction waste and manufacturing method of lightweight environment-friendly brick

A technology of construction waste and manufacturing method, applied in the field of building bricks, to achieve the effect of protecting environmental resources and realizing resource recycling

Inactive Publication Date: 2021-09-03
华厦筑工(广东)科技有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to provide a light-weight environmentally friendly brick made of construction waste and its manufacturing method, to solve the existing problem: with the increasing demand for building bricks, there is an urgent need to better solve the demand for bricks , and reduce the harm to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] The technical solutions in the embodiments of the present invention will be clearly and completely described below. Obviously, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0037] The present invention is a kind of lightweight environment-friendly brick made from construction waste and its manufacturing method, which is characterized in that it is made of the following raw materials in weight ratio:

[0038] Soil component particles (5mm ~ 100mm) 1 ~ 5 parts

[0039] 20-30 parts of construction waste coarse particles (3mm-5mm)

[0040] 20-30 parts of construction waste fine particles (0.5mm-3mm)

[0041] Garbage ash powder (below 0.5mm) 10-25 parts

[0042] 10-15 parts of fly ash

[0043] Cement: 5-10 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a lightweight environment-friendly brick manufactured from construction waste and a manufacturing method of the lightweight environment-friendly brick, and relates to the technical field of building bricks. The lightweight environment-friendly brick is characterized by being prepared from the following raw materials in parts by weight: 1-5 parts of soil component particles (5mm-100mm), 20-30 parts of construction waste residue coarse particles (3mm-5mm), 20-30 parts of construction waste residue fine particles (0.5 mm-3mm), 10-25 parts of garbage ash powder (0.5 mm or below), 10-15 parts of fly ash, 5-10 parts of cement, 8-13 parts of calcium oxide, 3-6 parts of calcium sulfate and 10-15 parts of water. Furthermore, the construction waste residues are waste concrete and mortar generated in the construction process. According to the lightweight environment-friendly brick produced from the construction waste residues and the garbage ash powder raw materials, the construction waste is turned into wealth, the requirement for using the brick is met, the harmful household garbage residues are treated, resource recycling of the waste materials is achieved, and then environment resources are protected.

Description

technical field [0001] The invention belongs to the technical field of building bricks, in particular to a light-weight environmentally friendly brick made from construction waste and a manufacturing method thereof. Background technique [0002] With the development of industry, the construction industry is also booming. During the construction of infrastructure, a large amount of construction waste will be generated. The accelerated development of urbanization has also increased the amount of urban solid waste. At the same time, domestic garbage Random discarding of the remaining residue after incineration will easily cause damage to the environment and bring safety hazards to the land and groundwater. With the acceleration of rural construction and development, the demand for building bricks is increasing, and there is an urgent need for better solutions. demand, and to reduce the harm of environmental pollution. Contents of the invention [0003] The object of the pres...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B18/16C04B18/10
CPCC04B28/00C04B18/16C04B18/10C04B2111/00017C04B18/08C04B22/064C04B22/143C04B14/04Y02W30/91
Inventor 胡志龙欧阳清瞿建国瞿雅莉
Owner 华厦筑工(广东)科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap