MSPC impregnated paper floor and preparation method thereof

A technology of impregnating paper and impregnating decorative paper, applied in chemical instruments and methods, paper/cardboard layered products, paper, etc., to achieve the effect of good scratch resistance, good wear resistance and improvement of load-bearing problems

Inactive Publication Date: 2021-10-08
ZHEJIANG SHENGLONG DECORATION MATERIAL
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a MSPC impregnated paper floor in order to solve the existing SPC floor performance defects such as scratch resistance, wear resistance, and cigarette burning resistance. The present invention combines the superior substrate of polyvinyl chloride with melamine impregnated paper, Obtain MSPC impregnated paper floor with good wear resistance and resistance to cigarette burning

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • MSPC impregnated paper floor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The present embodiment provides a preparation method of MSPC impregnated paper floor, and the preparation method comprises the following steps:

[0033] 1) Immerse the impregnated decorative paper layer into the first glue and the second glue, and then coat the surface of the impregnated decorative paper layer and the SPC base material layer with the hot-press bonding resin ESA-8180A, and the coating amount of the hot-press bonding resin 15g / m 2 , obtain the MSPC material layer; wherein, the first glue includes by weight: 28 parts of urea, 60 parts of formaldehyde and 5 parts of auxiliary agent A, and the used auxiliary agent A is a penetrant; the second glue includes by weight: 45 parts of melamine parts, 40 parts of formaldehyde, 7 parts of water and 3 parts of auxiliary agent B, the auxiliary agent B used is an anti-sticking agent, a mold release agent and a dustproof agent with a mass ratio of 3:1:2; the coating weight of the first glue is 66g / m 2 , the coating w...

Embodiment 2

[0037] The present embodiment provides a preparation method of MSPC impregnated paper floor, and the preparation method comprises the following steps:

[0038] 1) Immerse the impregnated decorative paper layer into the first glue and the second glue, and then coat the surface of the impregnated decorative paper layer and the SPC base material layer with the hot-press bonding resin ESA-8180A, and the coating amount of the hot-press bonding resin 17g / m 2 , obtain the MSPC material layer; wherein, the first glue includes by weight: 35 parts of urea, 65 parts of formaldehyde and 7 parts of auxiliary agent A, and the used auxiliary agent A is a penetrant; the second glue includes by weight: 30 parts of melamine parts, 52 parts of formaldehyde, 15 parts of water and 8 parts of auxiliary agent B, the auxiliary agent B used is an anti-sticking agent, a release agent and a dust-proof agent with a mass ratio of 3:1:2; the coating amount of the first glue is 72g / m 2 , the coating weigh...

Embodiment 3

[0042] The present embodiment provides a preparation method of MSPC impregnated paper floor, and the preparation method comprises the following steps:

[0043] 1) Immerse the impregnated decorative paper layer into the first glue and the second glue, and then coat the surface of the impregnated decorative paper layer and the SPC base material layer with the hot-press bonding resin ESA-8180A, and the coating amount of the hot-press bonding resin 13g / m 2 , obtain the MSPC material layer; wherein, the first glue includes by weight: 30 parts of urea, 50 parts of formaldehyde and 6 parts of auxiliary agent A, the used auxiliary agent A is a penetrant, and the second glue includes by weight: melamine 35 parts, 45 parts of formaldehyde, 10 parts of water and 5 parts of auxiliary agent B; the auxiliary agent B used is an anti-sticking agent, a mold release agent and a dustproof agent with a mass ratio of 3:1:1.5; the coating amount of the first glue is 69.6 g / m 2 , the coating weigh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an MSPC impregnated paper floor and a preparation method thereof. The MSPC impregnated paper floor sequentially comprises a wear-resistant paper layer, an impregnated decorative paper layer, an MSPC material layer, an SPC base material layer, an MSPC material layer and a balance paper layer, wherein the preparation method of the MSPC material layer comprises the steps that the impregnated decorative paper layer and the balance paper layer are soaked in first glue and second glue correspondingly, then hot-pressing laminating resin is coated on the surface, opposite to the SPC base material layer, of the impregnated decorative paper layer, and hot-pressing laminating resin is coated on the surface, opposite to the SPC base material layer, of the balance paper layer to obtain the MSPC material layer. The MSPC impregnated paper floor provided by the invention has the advantages of good scratch resistance, good wear resistance and cigarette burning resistance; according to the MSPC impregnated paper floor, the excellent performance of the surface of a laminate floor is combined with an SPC base material, the comprehensive performance of a ceramic tile is achieved, the MSPC impregnated paper floor can replace ceramic tiles, marble, solid wood and other rare materials, the cost of raw materials is reduced, and the MSPC impregnated paper floor can resist boiling for 2 hours at 100 DEG C or 4 hours at 90 DEG C after being attached and does not have the problems of bubbling, cracking and layering.

Description

technical field [0001] The invention belongs to the field of flooring, and relates to an SPC floor, in particular to an MSPC impregnated paper floor with good wear resistance, resistance to cigarette burning, energy saving and emission reduction, and reduction of raw material cost and processing cost, and a preparation method thereof. Background technique [0002] Flooring, the surface layer of the ground or floor of a house. Made of wood or other materials. There are many classifications of floors. According to the structure, they are: solid wood floors, laminate floors, three-layer solid wood floors, bamboo floors, anti-corrosion floors, cork floors, and the most popular multi-layer solid wood composite floors. Classification by use: Household, commercial, anti-static floor, outdoor floor, special floor for stage dance, special floor for sports venues, special floor for track and field, etc.; classified by environmental protection level: E0 floor, E1 floor, F4 floor, JAS ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F15/02E04F15/10E04F15/18D21H17/06D21H17/07D21H17/51B32B27/10B32B27/18B32B29/00B32B29/06B32B33/00B32B37/10B32B38/08
CPCE04F15/02E04F15/107E04F15/181D21H17/72D21H17/06D21H17/07D21H17/51B32B29/00B32B29/06B32B29/005B32B27/10B32B27/18B32B33/00B32B37/10B32B38/08B32B2255/12B32B2255/10B32B2255/26B32B2307/554
Inventor 盛英明吕妙玲李洪丽周杨
Owner ZHEJIANG SHENGLONG DECORATION MATERIAL