A kind of water quenching lining board and its preparation method and application

A technology for water quenching and lining, which is applied in the field of coke quenching lining, can solve the problems of limited performance such as hardness, toughness and high temperature wear resistance of water quenching lining, so as to improve hardness, reduce production cost and improve quenching. The effect of permeability

Active Publication Date: 2022-05-20
山西滨腾机械有限公司 +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the defects of limited hardness, toughness and high temperature wear resistance of the existing water quenching liner, and further provide a water quenching liner and its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water quenching lining board and its preparation method and application
  • A kind of water quenching lining board and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] This embodiment provides a method for preparing a water quenching liner, which includes the following steps:

[0025] 1) Weigh the raw materials of each component according to the proportion of the formula, and then add No. 18 bread iron in the intermediate frequency electric furnace for smelting. After the bread iron is melted, add carbon particles, ferrochromium, ferronickel, ferrosilicon, ferromanganese, ferromolybdenum, Metal antimony and rhenium are smelted to obtain the molten steel. The components of the molten steel are: C: 2.9%, Cr: 3.0%, Ni: 0.7%, Si: 2.9%, Mn: 1.2%, Mo: 0.4%, Re: 0.12%, Sb: 0.06%, P: 0.01%, S: 0.006%, the rest is Fe and other unavoidable impurities;

[0026] 2) Pour molten steel into a forming mold through a pouring device to cool and form it to obtain a rough billet for a water quenching coke lining plate, the rough billet has a thickness of 25 mm, a width of 400 mm, and a length of 900 mm;

[0027] 3) Heat the rough blank of the water quen...

Embodiment 2

[0029] This embodiment provides a method for preparing a water quenching liner, which includes the following steps:

[0030] 1) Weigh the raw materials of each component according to the proportion of the formula, and then add No. 18 bread iron in the intermediate frequency electric furnace for smelting. After the bread iron is melted, add carbon particles, ferrochromium, ferronickel, ferrosilicon, ferromanganese, ferromolybdenum, Metal antimony and rhenium are smelted to obtain the molten steel. The components of the molten steel are: C: 2.7%, Cr: 3.4%, Ni: 0.6%, Si: 3.0%, Mn: 1.7%, Mo: 0.6%, Re: 0.15%, Sb: 0.05%, P: 0.009%, S: 0.008%, the rest is Fe and other unavoidable impurities;

[0031] 2) Pour molten steel into a forming mold through a pouring device to cool and form it to obtain a rough billet for a water quenching coke lining plate, the rough billet has a thickness of 25 mm, a width of 400 mm, and a length of 900 mm;

[0032] 3) Heat the rough blank of the water que...

Embodiment 3

[0034] This embodiment provides a method for preparing a water quenching liner, which includes the following steps:

[0035] 1) Weigh the raw materials of each component according to the proportion of the formula, and then add No. 18 bread iron in the intermediate frequency electric furnace for smelting. After the bread iron is melted, add carbon particles, ferrochromium, ferronickel, ferrosilicon, ferromanganese, ferromolybdenum, Metal antimony and rhenium are smelted to obtain the molten steel. The components of the molten steel are: C: 3.1%, Cr: 2.2%, Ni: 0.9%, Si: 1.7%, Mn: 0.6%, Mo: 0.3%, Re: 0.1%, Sb: 0.08%, P: 0.007%, S: 0.009%, the rest is Fe and other unavoidable impurities;

[0036] 2) Pour molten steel into a forming mold through a pouring device to cool and form it to obtain a rough billet for a water quenching coke lining plate, the rough billet has a thickness of 25 mm, a width of 400 mm, and a length of 900 mm;

[0037] 3) Heat the rough billet of the water que...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of coke quenching lining boards, in particular to a water coke quenching lining board and its preparation method and application. The water quenching lining plate provided by the present invention includes the following chemical components in mass percentage: C: 2.7-3.1%, Cr: 2.2-3.4%, Ni: 0.6-0.9%, Si: 1.7-3.0%, Mn: 0.6- 1.7%, Mo: 0.3‑0.6%, Re: 0.1‑0.15%, Sb: 0.05‑0.08%, P≤0.02%, S≤0.02%, and the rest are Fe and other unavoidable impurities. The water quenching coke lining plate provided by the present invention adopts the design concept of low Cr and low C, and at the same time, a specific amount of Re and Sb is added to the alloy material. It is beneficial to improve the hardness, toughness, high temperature wear resistance and other properties of the liner, and can also greatly reduce the production cost.

Description

technical field [0001] The invention relates to the technical field of coke quenching lining boards, in particular to a water coke quenching lining board and its preparation method and application. Background technique [0002] The coke quenching coke tank car is the supporting equipment of the coke oven. It generally runs on the track below the coke side of the coke oven. Coke, and finally transport the extinguished coke to the designated place. At present, there are mainly two coke quenching methods: water quenching and dry coke quenching. In the process of water coke quenching, the lining board of the coke quenching car needs to periodically withstand the high temperature impact and wear when red coke is loaded into the car. The hardness, toughness and high temperature wear resistance of the water quenching liner put forward higher requirements. [0003] Common gray cast iron and nodular milled cast iron are mostly used as materials for water quenching coke linings at p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C37/08C22C37/10C21C1/08C21D1/773C21D5/00C21D9/00C22C33/08C10B39/04C10B39/14
CPCC22C37/08C22C37/10C22C33/08C21C1/08C21D1/773C21D9/0068C21D5/00C10B39/04C10B39/14Y02P20/129
Inventor 崔占斌
Owner 山西滨腾机械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com