A decorative board and its preparation process

A preparation process and a technology for decorative boards, which are applied in decorative arts, processes for producing decorative surface effects, protein coatings, etc., can solve the problems of easy damage of decorative paper, high technical requirements, and difficult process, and reduce costs. , The effect of low process difficulty and high efficiency

Active Publication Date: 2022-05-10
山东东宇鸿翔装饰材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the above technical problems, the present invention provides a decorative board and its preparation process, which solves the problem that the preparation of a decorative board with a three-dimensional relief texture effect in the prior art can only be realized by using a one-to-one steel plate relief mold; at the same time, it solves the problem of steel plate mold and decorative The decorative paper is easily damaged, the process is difficult, and the technical requirements are high due to paper synchronous sleeve pressing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A decorative board and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Embodiment 1 A kind of preparation method of polymer water-based resin material

[0036] A polymer water-based resin material, comprising the following components by weight:

[0037] 16 parts of toughening resin, 4 parts of water-based silicone additives, 4 parts of matting agent, 5 parts of casein, 5 parts of curing agent, 6 parts of dispersing agent, 5 parts of release agent, 30 parts of ethanol, and 25 parts of water.

[0038] Described toughening resin is aqueous polyvinyl chloride emulsion, and model is Stc4, is produced by German domo company, is made of modified polyvinyl chloride, modified polyvinyl alcohol, modified silicon dioxide, methyl methacrylate, butyl fat, It is made of acrylic acid, trimethylhexadecyl amine, hydrophilic silica and other materials.

[0039] Described water-based organosilicon auxiliary agent: the water-based organosilicon auxiliary agent that model is XZ-GY25, produced by Shanghai Kaiyin Chemical Industry;

[0040] The delustering age...

Embodiment 2

[0051] Embodiment 2 A kind of preparation method of polymer water-based resin material

[0052] A polymer water-based resin material, comprising the following components by weight:

[0053] 18 parts of toughening resin, 3.5 parts of water-based silicone additives, 4.5 parts of matting agent, 6 parts of casein, 5.5 parts of curing agent, 5 parts of dispersant, 4 parts of release agent, 28 parts of ethanol, and 27 parts of water.

[0054] Described toughening resin is aqueous polyvinyl chloride emulsion, and model is Stc4, is produced by German domo company, is made of modified polyvinyl chloride, modified polyvinyl alcohol, modified silicon dioxide, methyl methacrylate, butyl fat, It is made of acrylic acid, trimethylhexadecyl amine, hydrophilic silica and other materials.

[0055] Described water-based organosilicon auxiliary agent: the water-based organosilicon auxiliary agent that model is XZ-GY25, produced by Shanghai Kaiyin Chemical Industry;

[0056] The delustering agent...

Embodiment 3

[0067] Embodiment 3 A kind of preparation method of polymer water-based resin material

[0068] A polymer water-based resin material, comprising the following components by weight:

[0069] 14 parts of toughening resin, 3.5 parts of water-based silicone additives, 3.5 parts of matting agent, 6 parts of casein, 4.5 parts of curing agent, 7 parts of dispersant, 6 parts of release agent, 32 parts of ethanol, and 23 parts of water.

[0070] Described toughening resin is aqueous polyvinyl chloride emulsion, and model is Stc4, is produced by German domo company, is made of modified polyvinyl chloride, modified polyvinyl alcohol, modified silicon dioxide, methyl methacrylate, butyl fat, It is made of acrylic acid, trimethylhexadecyl amine, hydrophilic silica and other materials.

[0071] Described water-based organosilicon auxiliary agent: the water-based organosilicon auxiliary agent that model is XZ-GY25, produced by Shanghai Kaiyin Chemical Industry;

[0072] The delustering age...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation process of a decorative board, comprising the following steps: preparing a polymer water-based resin material; mixing water-based ink with a polymer water-based resin material to prepare a polymer water-based resin composite material; preparing a polymer water-based resin material; The raw materials used in the resin material include toughening resin, water-based silicone additives, matting agent, casein, curing agent, dispersant, mold release agent, ethanol, and water. The decorative paper with wood grain texture is obtained by printing with the polymer water-based resin composite material, and dipped in glue to obtain the dipped paper; the decorative board with three-dimensional relief texture effect is obtained by compression molding with a flat mold. The method solves the problem that a relief mold must be used to prepare a decorative plate with a three-dimensional relief texture effect in the prior art, and a relatively high temperature and a relatively high pressure are required.

Description

technical field [0001] The invention belongs to the field of decorative board preparation technology, and in particular relates to a decorative board and a preparation technology thereof. Background technique [0002] With the development and progress of society, consumers' life satisfaction and pursuit of quality of life are getting higher and higher, and the requirements for visual effects of furniture decoration products have also increased. Therefore, for furniture decorative boards, having a three-dimensional relief texture effect is more and more popular. In order to prepare a decorative plate with a three-dimensional relief texture effect, the existing process is to prepare a steel plate mold corresponding to the target texture relief effect, which requires a one-to-one matching of the decorative plate and the steel plate mold. [0003] The production process of the decorative board with three-dimensional embossed texture effect is as follows: (1) First, print the wo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline