Corner connecting material for bonding ethylene-propylene-diene monomer rubber, and preparation method thereof

A technology of EPDM rubber and corner material, which is applied in the field of corner material, and can solve the problem of weak bonding of thin and narrow edges of materials

Pending Publication Date: 2021-12-17
张家港市美特高分子材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The first technical problem to be solved by the present invention is to provide a corner joint material for bonding EPDM rubber. The problem of poor bonding of the thin and narrow edges of the material
[0005] The second technical problem to be solved by the present invention is to provide a method for preparing corner joints for bonding EPDM rubber. The problem of poor bonding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Corner connecting material for bonding ethylene-propylene-diene monomer rubber, and preparation method thereof
  • Corner connecting material for bonding ethylene-propylene-diene monomer rubber, and preparation method thereof
  • Corner connecting material for bonding ethylene-propylene-diene monomer rubber, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] Above-mentioned a kind of preparation method that is used for bonding the corner material of EPDM rubber, comprises the following steps:

[0039] 1) Add naphthenic oil to ultra-high molecular weight SEBS for oil extension, and the standing time after oil extension is 5-10h;

[0040] 2) Weigh polypropylene and EPDM rubber into the SEBS filled with oil in step 1), mix in a low mixer for 5-10min, and mix evenly;

[0041] 3) Weigh erucamide, silicone masterbatch, antioxidant and black masterbatch and add to the mixture in step 2), mix in a low mixer for 10-20min, and mix thoroughly;

[0042] 4) Weigh talcum powder and add it to the mixture in step 3), mix it in a low mixer for 10-20mim, and mix thoroughly;

[0043] 5) Add the mixed material in the above step 4) into the twin-screw by feeding, melt in the twin-screw and extrude through the machine head. Granulate in the granulator to obtain the product, wherein the temperature setting of the twin-screw zone is 60°C, 80°C, ...

Embodiment 1

[0046] A kind of joint material that is used for bonding EPDM of ternary ethylene propylene rubber, by weight, comprises the following components:

[0047]

[0048]

[0049] The above-mentioned preparation method of the thermoplastic elastomer corner material for bonding EPDM rubber may further comprise the steps:

[0050] 1) Add naphthenic oil to ultra-high molecular weight SEBS for oil extension, and the standing time after oil extension is 10h;

[0051]2) Weighing polypropylene and EPDM rubber into the SEBS filled with oil in step 1), mixing in a low mixer for 8 minutes, and mixing evenly;

[0052] 3) Weigh erucamide, silicone masterbatch, antioxidant and black masterbatch and add to the mixture in step 2), mix in a low mixer for 10 minutes, and mix thoroughly;

[0053] 4) Weigh the filler and add it to the mixture in step 3), mix it in a low mixer for 10 minutes, and mix thoroughly;

[0054] 5) Add the mixed material in the above step 4) into the twin-screw by feed...

Embodiment 2

[0056] A kind of joint material for bonding EPDM rubber, by weight, includes the following components:

[0057]

[0058]

[0059] The preparation method of the scrap material of the present embodiment 2 is the same as that of the embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a corner connecting material for bonding ethylene-propylene-diene monomer rubber. The corner connecting material comprises, by weight, 13-20 parts of polypropylene; 3-10 parts of ethylene-propylene-diene monomer rubber; 25-35 parts of ultra-high molecular weight SEBS; 25-30 parts of naphthenic oil; 0.1-0.3 part of erucyl amide; 1-5 parts of silicone master batch; 0.1-0.3 part of an antioxidant; 10-18 parts talcum powder; and 1-3 parts of black master match. The corner connecting material for bonding the ethylene-propylene-diene monomer rubber is high in bonding strength and good in using effect.

Description

technical field [0001] The present invention relates to a corner material, in particular to a corner material for bonding EPDM rubber and a preparation method thereof. Background technique [0002] EPDM rubber is an elastomeric material polymerized from ethylene and propylene monomers by adding a small amount of non-conjugated diene. It is characterized in that there are no unsaturated double bonds in the polymer molecular chain, and unsaturated double bonds are introduced into the branch chain. , because of its excellent weather resistance, heat resistance, ozone resistance, acid and alkali resistance, chemical corrosion resistance, excellent processing performance and low compression set, it is the preferred material for the production of automotive sealing strips. [0003] There are a large number of manufacturers in the automotive sealing strip industry, and the requirements for the sealing strip industry are getting higher and higher. It is a domestic problem to apply t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L53/02C08L91/00C08L23/12C08L23/16C08L83/04C08K5/20C08K3/34
CPCC08L53/025C08L91/00C08L23/12C08L23/16C08L83/04C08K5/20C08K3/34
Inventor 钟明杨新星
Owner 张家港市美特高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com