A high-strength, artificial leather technology, applied in the field of artificial leather, can solve the problems of poor surface wear resistance, easy wear and tear, easy to appear scratches, etc., and achieve the effect of simple structure, convenient operation and good effect

Pending Publication Date: 2022-03-11
苏州市广得利橡塑有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] There are certain disadvantages in the existing artificial leather in use. First of all, when the artificial leather is used, the surface wear resistance is not good, there is no coating, and it is prone to scratches, which is not conducive to pe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0022] Example 1:

[0023] High-strength wear-resistant coated artifact art, including fabric base fabric, gel coating, foam film, artificially synthetic high molecular weight polymer, phthalate, surface coated material, high strength composite film, fabric base The cloth has a share of 20-30%. The gel coating is 6-12%, and the proportion of the foamed film is 10-15%, and the composition of the artificial synthetic high molecular weight polymer is 10-20%, phthalic acid. The part of dibutyl is 8-16%, the surface coated material is 9-18%, and the high-strength composite film has a share of 10-20%.

[0024] Further, the fraction of the fabric base fabric is 28%, the gel coating is 9%, the proportion of the foaming film is 10%, the composition of the manual synthetic high molecular weight polymer is 15%, dibutyl phthalate The share was 13%, the surface coated material was 14%, and the high strength composite film was 11%.

[0025] A high-strength wear-resistant coating artificial leat...

Example Embodiment

[0034] Example 2:

[0035] On the basis of the first example, a high-strength wear-resistant coated artifact, including fabric base fabric, gel coating, foamed film, manual synthetic high molecular weight polymer, phthalate, surface coating material With the high-strength composite film, the fabric base fabric is 20-30%, the gel coating is 6-12%, the proportion of the foaming film is 10-15%, and the share of the manual synthetic high molecular weight polymer is 10 -20%, the dibutyl phthalate was 8-16%, and the surface coating material was 9-18%, and the high strength composite film was 10-20%.

[0036] Further, the fraction of the fabric base fabric is 25%, the deposition of the gel coating is 10%, the deposit film is 11%, and the proportion of high molecular weight polymer in the artificial synthesis of 16%, dibutyl phthalate The share is 11%, the surface coating material is 15%, and the high strength composite film is 12%.

[0037] A high-strength wear-resistant coating artifici...

Example Embodiment

[0046] Example 3:

[0047] Based on the embodiments, a high-intensity wear-resistant coated artifact, including fabric base fabric, gel coating, a foamed film, artificially synthesis high molecular weight polymer, dibutyl phthalate The surface coated material and the high-strength composite film, the fraction of the fabric base fabric is 20-30%, the deposition of the gel coating is 6-12%, the proportion of the foam film is 10-15%, and the manual synthesis of high molecular weight polymer The share was 10-20%, the divitric dibutyl phthalate was 8-16%, and the surface coated material was 9-18%, and the high strength composite film was 10-20%.

[0048] Further, the fraction of the fabric base fabric is 28%, the gel coating is 9%, the proportion of the foaming film is 10%, the composition of the manual synthetic high molecular weight polymer is 15%, dibutyl phthalate The share was 13%, the surface coated material was 14%, and the high strength composite film was 11%.

[0049] A high-s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses high-strength wear-resistant coated artificial leather and a preparation method thereof.The high-strength wear-resistant coated artificial leather comprises 20-30% of fabric base cloth, 6-12% of a gel coating, 6-12% of a foaming film, 5-10% of an artificially synthesized high-molecular-weight polymer, 5-10% of dibutyl phthalate, 5-10% of a surface coating material and 5-10% of a high-strength composite film. The proportion of the foaming film is 10-15%, the proportion of the artificially synthesized high molecular weight polymer is 10-20%, the proportion of the dibutyl phthalate is 8-16%, the proportion of the surface coating material is 9-18%, and the proportion of the high-strength composite film is 10-20%. According to the high-strength wear-resistant coated artificial leather and the preparation method thereof, the surface coating film and the high-strength composite film are arranged, so that the surface wear resistance of the artificial leather can be improved, the surface is prevented from being scratched, the service life is prolonged, the use strength of the artificial leather can also be improved, and the high-strength wear-resistant coated artificial leather has a very good tear-resistant effect; and the use performance is more excellent.

Description

technical field [0001] The invention relates to the field of artificial leather, in particular to a high-strength wear-resistant coated artificial leather and a preparation method thereof. Background technique [0002] Artificial leather is a kind of artificially manufactured plastic product. Due to the different synthetic resins used in artificial leather, different types of substrates, different production methods, whether there is foaming and different uses, artificial leather can be divided into many types. With the development of science and technology With continuous development, people have higher and higher requirements for the manufacturing process of artificial leather. [0003] There are certain disadvantages in the existing artificial leather in use. First of all, when the artificial leather is used, the surface wear resistance is not good, there is no coating, and it is prone to scratches, which is not conducive to people's use. When used, the strength may be p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B5/02B32B5/18B32B5/24B32B9/00B32B9/04B32B27/08B32B27/30B32B27/34B32B27/32B32B33/00B32B37/00B32B37/10B32B37/06B32B38/06
CPCB32B5/02B32B5/18B32B5/245B32B9/00B32B9/04B32B27/08B32B27/304B32B27/34B32B27/322B32B33/00B32B37/00B32B37/10B32B37/06B32B38/06B32B2037/243B32B2255/10B32B2255/02B32B2255/26B32B2307/554B32B2307/5825B32B2307/3065
Inventor 沈息宇
Owner 苏州市广得利橡塑有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap