Manufacturing process of antioxidant iron-made handicraft

A technology for making crafts and handicrafts, applied in decorative arts, special decorative structures, etc., can solve problems such as easy to fall off, affect the comfort of use, and poor adhesion of anti-oxidation coatings

Pending Publication Date: 2022-04-05
福州迈吉家居有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the iron products in the prior art adopt an integrated anti-oxidation manufacturing process, and the anti-oxidation coating has poor adhesion, which is easy to fall off and affects the comfort of use, resulting in poor anti-oxidation ability of the finished product, and a short period of anti-oxidation for iron handicrafts.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing process of antioxidant iron-made handicraft
  • Manufacturing process of antioxidant iron-made handicraft

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] The technical solutions of the present invention will be further described below in conjunction with the accompanying drawings and through specific implementation methods.

[0037] A kind of anti-oxidation iron handicraft manufacturing process provided by the present invention, comprises a kind of anti-oxidation iron handicraft manufacturing process provided by the present invention, comprises the following steps:

[0038] Include the following steps:

[0039] S01 Forming: first process and shape the iron handicraft;

[0040] S02 preparation: mix the hard iron flakes, put the hard iron flakes into the special spray gun 3;

[0041] S03 Spraying for the first time: install a special spray gun 3 on the spraying machine to spray the iron handicraft, so that the surface of the iron handicraft forms several irregular grooves due to the impact of the hard iron sheet;

[0042] S04 coating: apply a layer of adhesive adhesive on iron crafts;

[0043] S05 Secondary spraying: Sp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing process of an anti-oxidation iron-made handicraft, belongs to the field of manufacturing processes, and aims to increase the anti-oxidation period of the iron-made handicraft by improving the flow of the manufacturing process of the anti-oxidation iron-made handicraft and improving the adhesion capacity of an anti-oxidation coating.

Description

technical field [0001] The invention relates to the field of manufacturing technology, in particular to a manufacturing technology of anti-oxidation iron handicraft. Background technique [0002] Iron is widely distributed in nature, but human beings discovered and utilized iron later than gold and copper. Because the natural elemental iron is very rare on the earth, and it is easy to oxidize and rust, and its melting point (1812K) is much higher than that of copper (1356K), which makes it more difficult to smelt than copper. The earliest iron discovered by mankind was the meteorite that fell from the sky. The percentage of iron contained in the meteorite is very high. It is a mixture of iron, nickel, cobalt and other metals. The method of melting iron ore has not yet come out, and it is impossible for human beings to obtain a large amount of pig iron. At that time, iron has always been regarded as the most precious metal with a mystery. With the development of time, peopl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B44C5/00
Inventor 卞祖铭庄江东庄江河
Owner 福州迈吉家居有限公司