Polypropylene beta crystal form compound nucleating agent and preparation method thereof
A technology of polypropylene and β crystal form, which is applied in the field of compound nucleating agent and preparation of polypropylene β crystal form, can solve the problems of poor compatibility of polypropylene and poor effect of improving polypropylene performance, and achieves the promotion of crystallization and organic growth. The effect of ordering and increasing the content of β crystals
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] Polypropylene beta crystal form compound nucleating agent: N'N-dicyclohexyl terephthalamide, polyethylene cyclophthalate, calcium stearate, isotactic polypropylene compound, the mass ratio is 1 :0.4:3:25; N'N-dicyclohexyl terephthalamide, polyethylene cyclophthalate and calcium stearate are mixed uniformly and then extruded with isotactic polypropylene to form a master batch.
[0021] Preparation of polypropylene: the above-mentioned polypropylene β crystal compound nucleating agent is added to polypropylene according to 0.1% of the mass of polypropylene, mixed, extruded and pelletized, and obtained by injection molding, wherein during injection molding, the melt temperature is controlled to 200 ° C , the injection rate is 40mm s -1 , injection pressure and holding pressure 40MPa, holding time 32s.
[0022] The β-crystal content is calculated by DSC test, the impact strength is based on GB / T1843-2008 for notched Izod impact strength, and GB / T 1634-2019 for thermal defo...
Embodiment 2
[0026] Polypropylene beta crystal form compound nucleating agent: N'N-dicyclohexyl terephthalamide, polyethylene cyclophthalate, calcium stearate, isotactic polypropylene compound, the mass ratio is 1 :0.3:2:20; N'N-dicyclohexyl terephthalamide, polyethylene cyclophthalate and calcium stearate are mixed uniformly and then extruded with isotactic polypropylene to form a master batch.
[0027] Preparation of polypropylene: the above-mentioned polypropylene β crystal compound nucleating agent is added to polypropylene according to 0.1% of the mass of polypropylene, mixed, extruded and pelletized, and obtained by injection molding, wherein during injection molding, the melt temperature is controlled to 200 ° C , the injection rate is 50mm s -1 , injection pressure and holding pressure 42MPa, holding time 30s.
[0028] Table 2 embodiment 2 experimental data
[0029] β crystal content Impact strength (kJ / m 2 )
Embodiment 3
[0031] Polypropylene beta crystal form compound nucleating agent: N'N-dicyclohexyl terephthalamide, polyethylene cyclophthalate, calcium stearate, isotactic polypropylene compound, the mass ratio is 1 :0.5:4:30; N'N-dicyclohexyl terephthalamide, polyethylene cyclophthalate and calcium stearate are mixed uniformly and then extruded with isotactic polypropylene to form a master batch.
[0032] Preparation of polypropylene: the above-mentioned polypropylene β-crystal compound nucleating agent is added to polypropylene according to 0.1% of the mass of polypropylene, mixed, extruded and granulated, and obtained by injection molding, wherein during injection molding, the melt temperature is controlled to 210 ° C , the injection rate is 45mm s -1 , injection pressure and holding pressure 42MPa, holding time 31s.
[0033] Table 3 embodiment 3 experimental data
[0034] β crystal content Impact strength (kJ / m 2 )
PUM
Property | Measurement | Unit |
---|---|---|
heat deflection temperature | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction