Curtain wall mounting component and material and manufacturing method thereof

A technology for installing parts and manufacturing methods, applied to walls, building components, buildings, etc., can solve problems such as reduced work efficiency, unstable installation, fracture failure, etc., to prevent curtain walls from falling, adapt to environmental changes, and have strong oxidation resistance Effect

Pending Publication Date: 2022-06-07
SHAOXING UNIV YUANPEI COLLEGE
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The structure of metal mounting parts has problems such as corrosion, fatigue, hydrogen embrittlement, etc., and it is prone to fracture and failure to cause falling off
The present invention has adopted POM to substitute metal material for this problem, but because the toughness of POM is poor, it is not suitable for long-term exposure outdoors
[0003] In the existing technology, during the installation process of the curtain wall, the beam frame will be nailed and fixed on the wall first, and then the curtain wall will be connected with the beam frame. During installation, holes will be punched on the beam frame according to the installation distance. Due to the deviation of the punching position and a certain inclination angle of the outer wall of the building, there is a certain error in the distance between the two curtain wall panels during actual installation. The previous position was relatively close, so the fixed position of the beam frame would be easily broken, resulting in unstable installation, and repeated drilling would also lead to a decrease in work efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Curtain wall mounting component and material and manufacturing method thereof
  • Curtain wall mounting component and material and manufacturing method thereof
  • Curtain wall mounting component and material and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A curtain wall installation component material, comprising the following components in percentage by mass:

[0042] POM 92.5wt%;

[0043] 4-Hydroxystyrene modified nitrile rubber 3.5wt%;

[0044] Anti-ultraviolet agent 1.5wt%;

[0045] Antioxidant 0.5wt%;

[0046] Compatibilizer 2wt%;

[0047] All components were blended in proportion and then added to an extruder for extrusion to obtain the material. The extruder nozzle temperature was 220°C, and the barrel temperature was 190°C.

Embodiment 2

[0049] A curtain wall installation component material, comprising the following components in percentage by mass:

[0050] POM 90wt%;

[0051] 4-hydroxystyrene modified nitrile rubber 5wt%;

[0052] Anti-ultraviolet agent 1.5wt%;

[0053] Antioxidant 0.5wt%;

[0054] Compatibilizer 3wt%;

[0055] All components were blended in proportion and then added to an extruder for extrusion to obtain the material. The extruder nozzle temperature was 220°C, and the barrel temperature was 190°C.

Embodiment 3

[0057] A curtain wall installation component material, comprising the following components in percentage by mass:

[0058] POM 95wt%;

[0059] 4-hydroxystyrene modified nitrile rubber 2wt%;

[0060] Anti-ultraviolet agent 0.5wt%;

[0061] Antioxidant 0.5wt%;

[0062] Compatibilizer 2wt%;

[0063] All components were blended in proportion and then added to an extruder for extrusion to obtain the material. The extruder nozzle temperature was 220°C, and the barrel temperature was 190°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of building curtain wall installation, and discloses a curtain wall installation component and a material and a manufacturing method thereof. The material of the mounting part comprises POM; an impact modifier; an anti-ultraviolet agent; an antioxidant; the curtain wall installation part is manufactured through a mold forming method, the curtain wall installation part comprises a curtain wall, a cross beam frame and an installation part body connecting the curtain wall and the cross beam frame, and the installation part body comprises an installation piece and two connecting pieces symmetrically distributed on the two sides of the installation piece. The invention overcomes the problem of rusting and fracture of metal, has high strength and small density, and can adapt to environmental change; and the mounting distance between the two curtain walls on the two sides can be adjusted, and mounting and adjusting convenience is improved.

Description

technical field [0001] The invention relates to the field of building curtain wall installation, in particular to a curtain wall installation component, a material and a manufacturing method thereof. Background technique [0002] In recent years, extreme weather has frequently occurred, causing the curtain wall to fall off frequently. The structure of metal mounting components has problems such as corrosion, fatigue, hydrogen embrittlement, etc., which are prone to fracture failure and fall off. The present invention adopts POM to replace the metal material to solve this problem, but due to the poor toughness of POM, it is not suitable for long-term exposure outdoors. [0003] In the prior art, during the installation process of the curtain wall, the cross-beam frame will be fixed on the wall by nails, and then the curtain wall and the cross-beam frame will be connected. Due to the deviation of the drilling position and a certain inclination angle of the outer wall of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04B2/96E04B2/88C08L59/00C08L15/00
CPCE04B2/965C08L59/00C08L15/00
Inventor 周长顺王琪栋蒋舸詹培敏
Owner SHAOXING UNIV YUANPEI COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com