Prepn. of composite nylon material capable of being blow moulded

A nylon composite material and nylon technology are applied in the field of preparation of blow moldable nylon composite materials, which can solve the problems of low melt strength of nylon 6, difficult to obtain ionic polymers, and difficulty in blow molding, and achieve broad application and industrialization prospects. , The effect of improving the melt strength and improving the impact toughness

Inactive Publication Date: 2004-11-24
SHANGHAI JIAOTONG UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Blow-molded polymers must have suitable melt strength and viscosity, but the usual nylon 6 has low melt strength and is difficult to blow mold
The United States, Japan and other countries have patents on nylon blow molding. Lavengood et al. (U.S.Pat.No.5,043,384) have adopted nylon 6 and ABS to blend to obtain blow-molded nylon. The comprehensive performance of this material is close to nylon 6, but It is not as good as nylon 6; Subramanian et al. used functionalized polyolefins and ionic polymers to obtain blown semi-crystalline nylon composites, but ionic polymers are difficult to obtain and costly (U.S. Pat. No. 5,122,570). Research on blow molding of nylon 6 involves less

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Mix 85% nylon 6, 0.3% TDI, 14.5% MAH-g-PP, 0.2% lanthanum oxide by weight under a high-speed mixer, and the speed of the high-speed mixer is 1200 rpm. It is processed in a twin-screw extruder. The screw speed is 300 rpm. The temperature of the screw feeding zone, plasticizing zone and mouth film are 210°C, 220°C, 235°C, 235°C, 235°C, 235°C, and 230°C respectively. and 225 ℃, the residence time of the material in the extruder is about 1.5 minutes, the extruded material is cooled in a cooling tank, and diced by a pelletizer to obtain pellets, which are dried in a vacuum oven at 110 ℃ for 24 hours. The material can be blow molded (such as a 500ml container), and its tensile strength, heat resistance, barrier properties, etc. have not changed, and its impact strength is twice that of the original nylon 6.

Embodiment 2

[0014] Mix 75% nylon 6, 1% ethylene glycol, 13% styrene-maleic anhydride copolymer (SMA), 10% ethylene-vinyl acetate copolymer (EVA), 1% samarium oxide by weight in a high-speed mixer Mix thoroughly and evenly, the speed of the high-speed mixer is 1000 rpm, and the mixed material is put into a twin-screw extruder for processing. 220°C, 225°C, 230°C, 235°C, 235°C, 230°C, 225°C and 220°C, the residence time of the material in the extruder is about 2 minutes, the extruded material is cooled in a cooling tank and pelletized Machine-cut pellets to obtain pellets, which were dried in a vacuum oven at 110° C. for 30 hours. The material can be blow molded, and its tensile strength and heat resistance are the same as those of the original nylon 6. The impact strength at room temperature is three times higher than that of the original nylon 6, and the low temperature impact strength is twice that of the original nylon 6. The oil leakage rate is higher than that of the original nylon 6. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

There is a method of preparing the inflatable nylon complex material, and the method is as follows; add the mixture of nylon 6, chain-expanding agent or functionalized polymer and rare-earth oxie which is evenly mixed in the high-speed stirrer into the common double-screw extruding machine, then make the things in the mixture reactively commix under a certain temperature and rotate speed then extrude the commixture and make the particles, and then obtained the inflatable nylon 6 material. The invention's method is simple, the made material retains the capability of original nylon 6 and at the same time improves the impactive tenacity, the strength of its melted body is high, and it can not only be injected to shape, but also be blowed into all kinds of hollow products with complicated shape, which make its applied range greatly enlarged.

Description

Technical field: [0001] The invention relates to a method for preparing a blow-moldable nylon composite material. A twin-screw extruder is used to reactively blend polycaprolactam, commonly known as nylon 6, with a small amount of chain extender or functionalized polymer to increase the melt strength of nylon. Greatly improved, so that nylon can be blow molded. The invention belongs to the technical field of polymer processing. Background technique: [0002] As we all know, polyamides are nylon polymers with excellent low temperature and high temperature performance, good mechanical properties, high tensile strength, excellent wear resistance, good self-lubrication, good impact toughness and high barrier properties. Chemical resistance and oil resistance are outstanding, so it has developed rapidly since its inception. Among them, polycaprolactam is nylon 6, which was invented by P. Schlach of I.G.Farbon Company in Germany in 1938. At first, nylon 6 was mainly used for syn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C47/40C08K3/22C08L77/00
Inventor 戚嵘嵘周持兴
Owner SHANGHAI JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com