Continuous torsion-less drawing process of producing steel wire with spiral rib

A spiral rib steel wire, operation production technology, applied in the field of steel wire production technology, can solve the problem of uneven mechanical properties of steel wire

Inactive Publication Date: 2002-05-22
北京中铁建协技术开发有限公司 +1
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this way, it not only improves the production efficiency and reduces the cost, but also effectively solves the problem of uneven mechanical properties of the steel wire caused by the equipment stoppage when the steel wire is stabilized at home and abroad, and the delay in the start-up of the intermediate frequency heating furnace. the quality of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Continuous torsion-less drawing process of producing steel wire with spiral rib
  • Continuous torsion-less drawing process of producing steel wire with spiral rib

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] Send the surface-treated wire rod 2 into the pay-off process I, which is equipped with two support type pay-off racks 1, and the tail of the wire rod 2 produced by online motion on one of the pay-off racks is the same as that on the other pay-off rack. The production wire rod 2 is docked; the butted wire rod 2 enters the multi-pass cold drawing plastic deformation process II, and the wire drawing equipment 4 in this process performs multi-pass cold drawing plastic deformation on the wire rod 2, and the stress adjustment device 3 Track and adjust the stress changes between different molds or caused by small changes in mold size. In order to avoid affecting the toughness of the wire due to plastic deformation and heating, this process is also equipped with water cooling facilities for wire drawing die sleeves; the water-cooled wire passes through the straightener 5 Entering the rotational plastic deformation process III, the rotor core of the rotational deformer 6 is embed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The continuous operation production line of spiral rib steel wire is formed by the procedures of paying-off, 1-8 multiple pass cold-drawing plastic deformation, rotating plastic deformation, medium-frequency heating stress-removing tempering, applying pretension, continuous feeding and reeling. The length of said production line is 60 m, and said production line can be controlled by microcomputer, its touch display screen and data display are clear and accurate, it adopts man-machine interface operation mode. It not only raises production efficiency, reduces production cost, but also raises quality of product, and effectively solves the difficult problem of non-uniform mechanical property of steel wire.

Description

Technical field: [0001] The invention is a new process for continuous production of low-relaxation spiral rib prestressed steel wire or smooth prestressed steel wire without torsion drawing, and belongs to the technical field of steel wire production technology. Background technique [0002] The production of low-relaxation prestressed steel wire at home and abroad is composed of three relatively independent processes of surface treatment, drawing and stabilization treatment. That is to say, the raw materials that have passed the inspection (non-twist-controlled cold Sorbitized wire rod) are put into production. The first process is surface treatment. The method is to remove the iron oxide scale on the surface of the wire blank and firmly coat it with good ductility. lubricant carrier. The second process is the drawing process. Put the wire blank after surface treatment on a single or continuous wire drawing machine, and carry out drawing plastic deformation in turn, and ob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21C1/16
Inventor 谢铁桥余景崎张秀云
Owner 北京中铁建协技术开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products