Metal powder paint and its production process

A metal powder and coating technology, applied in powder coatings, polyester coatings, epoxy resin coatings, etc., can solve the problems of easy combustion, explosion, large amount of addition, different effects, etc., to improve safety protection, inhibit metal Combustion, the effect of simple production operation

Inactive Publication Date: 2004-09-08
顺德市均安镇蓝天实业有限公司 +1
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method is prone to safety accidents such as combustion and explosion during the production process, and the metal powder coating produced is unevenly dispersed, and the amount of addition is large, which requires high spraying equipment, affects the spraying effect, and is likely to cause inconsistent effects.
Also because the metal substance has not been processed, during the extrusion process, due to the shear force of the screw, the original arrangement structure of the metal substance is destroyed, and the original metal performance effect is lost, so that the original effect of the metal powder coating cannot be achieved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] First, heat 0.5 parts of wax powder (BASF) to 300°C, let the wax become molten, and then slowly add 3 parts of fine gold powder (particle size below 7um) Powdersafel 790-01 (ECKART) to the melted In the wax liquid, stir at high speed under the action of ultrasonic waves for 20 minutes. After standing for 3 hours, filter and separate the melted wax liquid. After cooling, crush the metal substance to obtain the required metal substance. Epoxy resin E-12 (domestic) 32 parts, resin 9011 (domestic) 33 parts, dispersant (domestic) 2 parts, leveling agent 503 (domestic) 5 parts, curing agent T105 (Nanhai Chemical Industry) 2 parts, filler BaSO 22 parts and 0.5 parts of color material are weighed and matched according to the weight, put into the mixing tank and mixed for 2 minutes, mixed evenly and then sent to the extruder to be extruded into flakes. The temperature of the feeding area of ​​the extruder is 90°C , the temperature in the extrusion zone is 100°C, the speed of the...

Embodiment 2

[0013] First heat 0.5 parts of wax powder (BASF) to 310°C to make the wax melt, then slowly add 3.5 parts of fine silver powder Powdersafel 080-01 (particle size below 7um) into the melted wax liquid , stirred at high speed for 2 to 3 minutes under the action of ultrasonic waves, and after standing for 4 hours, filtered and separated the melted wax liquid, and after cooling, crushed the metal substance to obtain the required metal substance, which was mixed with polyurethane 2598 (Tiansong) 65 parts, curing agent T105 (Nanhai Chemical Industry) 2.7 parts, leveling agent 503 (domestic) 5 parts, dispersant (domestic) 2 parts, filler BaSO 20.8 parts, and coloring material 0.5 parts Weigh and mix according to the weight , put them together in the mixing tank for 3 minutes, mix evenly, and then transport them to the extruder to be extruded into flakes. The speed of the main engine is 1400 rpm, the feeding speed is 35 rpm, and then it is crushed at a high speed by the pulverizer. Th...

Embodiment 3

[0015] First, heat 0.5 parts of wax powder (BASF) to 320°C to make the wax melt, then slowly add 2 parts of fine gold powder Powdersafel 785-01 (ECKART) and 2 parts of silver powder Powdersafel 080-01 (ECKART) Add it into the melted wax liquid (their particle size is below 7um), stir at a high speed for 25 minutes under the action of ultrasonic waves, and after standing for 5 hours, filter and separate the melted wax liquid, and conduct metal substances after cooling The required metal substance can be obtained after crushing, mix it with 65 parts of polyurethane 1200 (South resin), 2 parts of dispersant, 2.5 parts of curing agent (B1530) and 0.5 part of curing agent CAB551-0.1 (Eastman), flow 4 parts of leveling agent, 21 parts of filler BaSO and 0.5 part of colorant are weighed and matched according to the weight, put into the mixing tank together for 4 minutes, mix evenly, transport to the extruder to be extruded into flakes, the extruder The temperature in the feeding zone...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistanceaaaaaaaaaa
adhesivityaaaaaaaaaa
Login to View More

Abstract

The metal powder paint consists of resin, wax coated metal powder, dispersant, curing agent, leveling agent, stuffing and small amount of pigment. The production process includes heating wax to 300-320 deg.c, adding fine metal powder slowly into the molten wax under high speed ultrasonic stirring, letting stand for 3-5 hr, filtering to separate, cooling and crushing to obtain coated metal mater; mixing the metal matter with the other components inside a mixing tank, extruding the mixture into sheet, crushing in a crusher, and sieving to obtain product of required grain size. The present invention has the advantages of inhibiting burning and explosion caused by friction of metal matter to raise the safety; dispersing the metal matter on the coated surface to produce metal effect, and simple production process.

Description

(1) Technical field [0001] The invention relates to a metal powder coating and a production method. (2) Background technology [0002] At present, in order to obtain metal powder coatings with metallic luster and special texture effects, they are generally obtained by adding metal, that is, adding metal substances in the post-sequence of powder coatings. This method is prone to safety accidents such as combustion and explosion during the production process, and the metal powder coating produced is unevenly dispersed, and the amount of addition is large, which requires high spraying equipment, affects the spraying effect, and is likely to cause inconsistent effects. . Also because the metal substance has not been processed, during the extrusion process, due to the shear force of the screw, the original arrangement structure of the metal substance is destroyed, and the original metal performance effect is lost, so that the original effect of the metal powder coating cannot be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/03C09D133/02C09D163/00C09D167/00C09D175/04
Inventor 何基财
Owner 顺德市均安镇蓝天实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com