Negative thermal-expansion coefficient adjustable laminated ceramic matrix composite and preparing method thereof

A negative thermal expansion coefficient, composite material technology, applied in ceramic layered products, chemical instruments and methods, layered products, etc., can solve the problems of difficult to control the negative expansion of multiphase materials, difficult to obtain compensation effects, complex sintering process, etc.

Inactive Publication Date: 2005-03-16
SHANGHAI JIAO TONG UNIV
View PDF2 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the sintering of this material is difficult to be dense. Although Merkel et al. have described in detail the use of various sintering aids to increase the density in the patent specification, t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Negative thermal-expansion coefficient adjustable laminated ceramic matrix composite and preparing method thereof
  • Negative thermal-expansion coefficient adjustable laminated ceramic matrix composite and preparing method thereof
  • Negative thermal-expansion coefficient adjustable laminated ceramic matrix composite and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] wxya 2 o 8 -20Vol.% SiO 2 laminated composite ceramic substrate

[0026] Prepare single-phase zirconium tungstate according to the following process: commercially available ZrO(NO 3 ) 2 Configured as 1M ZrO(NO 3 ) 2 solution, and configure 1M ammonia complex (NH 4 ) 6 h 2 W 12 o 40 etc. as precursors, these precursors are uniformly mixed according to the atomic ratio of the metals contained in Zr:W=1.0:2.0, heated in a water bath at 60-80°C with constant stirring, and titrated with 2M acetic acid solution into the mixed precursors until A uniform colloidal precipitate containing W and Zr was completely formed. The resulting colloidal precipitate was washed and dehydrated to form a wet gel. Keep warm at 1100-1150°C for 2-4 hours, then quickly quench to room temperature, mix the obtained product with absolute ethanol and ball mill for 4 hours, repeat the above-mentioned process of calcination and quenching to room temperature 1-2 times, the calcination tempera...

Embodiment 2

[0031] 0.4mol% Y 2 o 3 -ZrW 2 o 8 / SiO 2 laminated composite ceramic substrate

[0032] Preparation containing 0.4mol% Y 2 o 3 The process of the zirconium tungstate solid solution powder is as follows: with commercially available Y 2 o 3 Dissolved in nitric acid solution, configured as 0.1M Y(NO 3 ) 3 solution, commercially available ZrO(NO 3 ) 2 Configured as 1M ZrO(NO 3 ) 2 solution, and configure 1M ammonia complex (NH 4 ) 6 h 2 W 12 o 40 etc. as precursors, these precursors are uniformly mixed according to the atomic ratio of the metals contained in Y: Zr: W = 0.008: 0.992: 2.0, heated in a water bath at 60-80°C with constant stirring, and titrated with 2M Acetic acid solution until a homogeneous colloidal precipitate containing various metal atoms is completely formed

[0033] With the above preparation containing 0.4mol% Y 2 o 3 Zirconium tungstate solid solution powder and commercially available amorphous silica powder are used as raw materials. T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a negative thermal-expansion coefficient adjustable laminated ceramic matrix composite and preparing method thereof consisting of, employing centrifugal casting and molding process, dispersing the negative expanding powder material whose component is cubic phase zirconium tungstate ZrW2O8 or doped and modified zirconium tungstate ZrW2O8 and near-zero expanding amorphous silicon oxide SiO2 powder into polyvinyl alcohol solution, so as to prepare zirconium tungstate powder slurry and silicon oxide powder slurry, employing a centrifugation deposition method to remove the water-based composition in the powder slurry, alternately depositing the zirconium tungstate powder and silicon oxide powder onto the filtration sheet, forming the blank of laminated composite material, finally proceeding high temperature sintering to obtain the compact laminated ceramic composite material.

Description

technical field [0001] The invention relates to a laminated ceramic matrix composite material with adjustable negative thermal expansion coefficient and a preparation method thereof. By adopting the method proposed by the invention, a series of ceramic matrix composite materials with adjustable negative thermal expansion coefficient can be obtained. The composite material can be used to manufacture substrates for thermal stability compensation packaging of optical fiber gratings, and belongs to the technical field of packaging materials for electronic or optoelectronic devices. Background technique [0002] Cubic phase zirconium tungstate ceramics, as a ceramic material with large isotropic negative expansion coefficient in a wide temperature range (0.3-1050K), has been extensively studied in recent years. Zirconium tungstate materials were first reported by J.Graham et al. in 1959 (J.Am.Ceram.Soc., 42, p570, 1959). In the 1960s, some documents also reported that zirconium t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B18/00C04B35/495C04B35/624
Inventor 孔向阳吴建生徐明钢
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap