Rare-earth, carbon and nitrogen co-permeating agent and its preparation

A technology of co-infiltration agent and rare earth, applied in the direction of metal material coating process, coating, solid-state diffusion coating, etc., can solve the problems that have not been reported yet

Inactive Publication Date: 2005-05-11
靳重滨
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using the method of chemical heat treatment to infiltrate rare earth elements on the metal surface through the solid-air interface, there is no report on the information currently available.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] The preparation method of the chemical puncture is as follows: (1) 8-20 grams of mixed rare earth chlorides are added to 1000 milliliters of methanol. Add 10-25 grams of ammonium chloride to 500 milliliters of formamide, and then add sodium to saturate the solution. (3) Mix the above with (1) and (2).

[0010] Adopt the prepared chemical infiltration of the present invention to 08 steel, GCrl5, 20CrHrn0, 1Xf just s, 18CrMnTi and other steels are carried out rare earth, carbon, nitrogen ternary co-infiltration, similar in its process conditions and conventional carbonitriding process, in Under laboratory conditions, more systematic data and good results in improving the properties of metal surfaces have been obtained. The scanning electron microscope energy measurement test shows that heavy and rare earths are not only enriched in the sub-grain boundaries, but also found in the grains. From the current research on rare earth in the metallurgical process, the test of rar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention was involved in infiltrated agent of Ti-Al co-diffusion and its preparation. The infiltrated agent consist of 10-25% TiO2,2-25% Al powder, 30-80% Al2O3,0.3-2.8% infiltrated agent. Infiltrated agent was NH4Cl or other halide. The method of infiltrated agent of Ti-Al co-diffusion adopted solid powder embedded infiltration technology and the infiltration temperature adopted ladder temperature. Firstly, the substance was heated to 650-900deg.C for 1-5h. Secondly, it was heated to 900-1150deg.C for 2-8h. The infiltration layer of Ti-Al co-diffusion could be finished by the invention and the infiltration layer was smooth, bright and with high corrosion resistance.

Description

technical field [0001] The invention relates to a catalyst, more specifically, it relates to a rare earth, carbon and nitrogen three-component co-infiltration chemical infiltration agent, which is a catalyst used for rare earth, carbon and nitrogen three-component co-infiltration on the surface of steel parts by chemical heat treatment. activator. Background technique [0002] The carbonitriding process has been widely used in the production of wear-resistant and fatigue-resistant parts such as power machinery, chemical machinery, automobiles, tractor gears, shafts and bearings. However, due to the commonly used carbon and nitrogen co-infiltration, the process still has the disadvantages of long production cycle, large energy consumption, and unstable process effect. [0003] The application of rare earth to the metal material industry has attracted close attention at home and abroad. The addition of rare earths to steel can improve the variou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C12/02
Inventor 靳重滨
Owner 靳重滨
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap