Process for improving viscosity of attapulgite clay

A technology for attapulgite clay and processing technology, which is applied in the directions of clay products, crystalline aluminosilicate zeolite, A-type crystalline aluminosilicate zeolite, etc., and can solve the problem of low improvement rate and the like

Inactive Publication Date: 2005-11-23
许庆华
View PDF1 Cites 107 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The disadvantage of the above invention is that the attapulgite clay produced by the "high-...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] Below in conjunction with embodiment the present invention will be further described:

[0022] 1. Natural weathering: The attapulgite clay mined from the mining area has a viscosity of 1800mPa·s. After 80 days of natural weathering, the viscosity of the attapulgite clay is 1880mPa·s, which is higher than that of the attapulgite clay just mined. Viscosity increased by 4.44%.

[0023] 2. Modification treatment:

[0024] ①Take 97% of attapulgite clay after natural weathering, add 3% sodium carbonate evenly, and input it into the immersion pool together, add clear water for immersion aging, and the immersion time is 96 hours.

[0025] ② Take the soaked attapulgite clay, put it into the mixer for stirring, and extrude the stirred attapulgite clay into thin slices through an extruder, and the thickness is controlled at 1.0 mm.

[0026] ③ The attapulgite clay thin slices are dried in the air, and the water content of the attapulgite clay thin slices after drying is ≤15%.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a jprocess for improving viscosity of attapulgite clay which comprises the steps of modification treatment, batching, agitating, milling and detect. The process can be applied into the real processing procedure of Attapulgite clay, and can increase the viscosity of the end product by over 35%.

Description

Technical field: [0001] The invention relates to a non-metallic ore processing technology, in particular to a processing technology for increasing the viscosity of attapulgite clay. Background technique: [0002] Attapulgite clay, also known as palygorskite or palygorskite, is a hydrous magnesium-rich silicate clay mineral with chain layer structure. Attapulgite clay has high plasticity in the presence of water, good stability in high temperature and salt water, and low density, generally 2.05-2.30g / cm 2 , hardness 2 to 3 (Mohs hardness). [0003] Due to the unique crystal structure of attapulgite, it has many special physical, chemical and technological properties, and has become one of the clay minerals with wide application and high economic value. Attapulgite clay is mainly used in water purification, adhesives, pesticide carriers, molecular sieves, desiccants, adsorbents, coatings, mud, activated clay, foundry sand and chemical industries. [0004] Attapulgite clay d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/04
Inventor 许庆华
Owner 许庆华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap