C5íóC9 copolymerized petroleum resin preparation method

A technology for copolymerizing petroleum resin and polymerization liquid, which is applied in the field of preparation of C5, C9 copolymerized petroleum resin, and can solve the problems of less copolymerization and the like

Inactive Publication Date: 2006-02-22
BC P INC CHINA NAT PETROLEUM CORP +1
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the existing petroleum resin patents, for C 9 There are many reports on petroleum resin, and C 5 、C 9 Copolymerized very little

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • C5íóC9 copolymerized petroleum resin preparation method
  • C5íóC9 copolymerized petroleum resin preparation method
  • C5íóC9 copolymerized petroleum resin preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Collect C with a boiling point of 40-70°C under normal pressure 5 Alkenes and C with a boiling point of 90-120°C at a vacuum of 0.09 MPa 9 Olefin component; first in the reactor with stirring (stirrer model is 60W, 3000 rpm, Changzhou Guohua Electric Machinery Co.), adding mass percentage is 10% toluene as solvent under the condition of being lower than 10 ℃ , then add 2% AlCl 3 Catalyst; Then in the toluene solvent with the speed of 2 drops / second dripping the C9 that the mass percentage is 30%, then with the speed of 1 drop / second in the toluene solvent, drop the C5 that the mass percentage is 60%; Dropping is completed After that, stir evenly, and react at 60°C for 6 hours to obtain a polymerization solution; pour the reacted polymerization solution into a separatory funnel and perform water washing-alkali washing-water washing at 75°C. It is a 5% NaOH solution, and this process is carried out alternately until the polymerization liquid is washed to neutral; pour t...

Embodiment 2

[0039] Collect C with a boiling point of 40-70°C under normal pressure 5 Alkenes and C with a boiling point of 90-120°C at a vacuum of 0.09 MPa 9 Olefin component; first in a stirred reactor, add 8% by mass of toluene as a solvent at a temperature lower than 10°C, and then add 1% by mass of AlCl 3 Catalyst; Then in the toluene solvent with the speed of 2 drops / second dripping mass percent is after the C9 of 33%, then in the toluene solvent with the speed of 1 drop / second is the C5 that drips the mass percent of 66%; Drops complete Afterwards, stir evenly, and react at 50°C for 5 hours to obtain a polymerization liquid; pour the reacted polymerization liquid into a separatory funnel and perform water washing-alkali washing-water washing at 65-75°C, and this process is carried out alternately until the polymerization liquid Washed to neutral; pour the polymer solution washed to neutral into the reactor, heat and distill the polymerization solution at 0.08Mpa, the heating temper...

Embodiment 3

[0041] Collect C with a boiling point of 40-70°C under normal pressure 5 Alkenes and C with a boiling point of 90-120°C at a vacuum of 0.09 MPa 9 Olefin component; first in a stirred reactor, add 9% by mass of toluene as a solvent at a temperature lower than 10°C, and then add 0.5% by mass of AlCl 3 Catalyst; Then in the toluene solvent with the speed of 2 drops / second dripping mass percent is after the C9 of 16%, then in the toluene solvent with the speed of 1 drop / second drips the C5 that the mass percent is 74.5%; Dropping is finished Afterwards, stir evenly, and react at 40°C for 3 hours to obtain a polymerization solution; pour the reacted polymerization solution into a separatory funnel and perform water washing-alkaline washing-water washing at 65°C, and this process is carried out alternately until the polymerization solution is washed to neutrality; pour the neutralized polymerization solution into the reactor, heat and distill the polymerization solution at 0.09Mpa,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
bromine numberaaaaaaaaaa
Login to view more

Abstract

Disclosed is a process for preparing C9 modified C5 petroleum resin, which comprises using C5 as the main raw material, using C9 as the modifying raw material, charging C9 active fraction into C5 active fraction, preparing C9 modified C5 petroleum resin, using AlCl3 as catalyst for copolymerizing C5, C9 petroleum resin.

Description

technical field [0001] The present invention relates to a kind of preparation method of petroleum resin, particularly a kind of C 5 、C 9 Preparation method of copolymerized petroleum resin. Background technique [0002] Petroleum resin was originally developed to replace pine resin and its derivatives. But once it came out, it developed rapidly. In just a few decades, it has already had a considerable production level and output. Especially in the industrially developed countries in the world, there are many specifications of petroleum resin products and the scale of production equipment is very large. For example, there are nine companies producing petroleum resin in Japan, with a production capacity of 1 million tons per year. Exxon, Hercules, and Goodyear in the United States; CdF in France; ICI in Britain and other major petrochemical companies in the world also have petroleum resin production devices. my country Taiwan and South Korea and other places also produce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F240/00
Inventor 李成贵李旭祥刘栓祥徐惠俭丁军程嘉杰张明非
Owner BC P INC CHINA NAT PETROLEUM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap