Ceramic wall tile surface treating agent

A surface treatment agent and wall brick technology, applied in the field of building materials, can solve problems affecting building renovation and maintenance, paint peeling, water seepage, etc. quality effect

Active Publication Date: 2006-06-28
李淦林
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the interface stress caused by the bonding between the paint and the mosaic and the tile and the difference in expansion coefficient, the paint will peel off, crack, seepage, etc.
Previously, there was not a good solution to this problem, which affected the renovation and maintenance of this type of buildings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] The present invention will be further described below with embodiment

[0008] Implementation one: first by weight percentage (%), natural washed yellow sand 43-47, Portland cement 40-30, polyvinyl alcohol (PVA) 11-13, methyl cellulose 5-8, high-strength polypropylene The ratio of fiber 1-2. Then mix the yellow sand and cement at a low speed in proportion, and then put in polyvinyl alcohol (PVA), methyl cellulose and polypropylene fiber and mix at a high speed for 30-40 minutes to make a putty ceramic wall tile surface treatment agent. After testing, the batches are qualified, measured and packaged for storage.

[0009] Implementation two: first by weight percentage (%) natural washing yellow sand 27-37, white cement 37-32, polyvinyl alcohol rubber powder (PVA) 11-13, methylcellulose 5-8, heavy calcium carbonate 20 -10 ratio, then mix natural washed yellow sand, white cement, and heavy calcium carbonate at a low speed according to the ratio, and then put in polyvinyl ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A surface treating agent for the adhesive surface of ceramic tile is prepared from inorganic silicate material, adhesive and multiple classes of aggregate. Its advantages are high adhesion, high toughness and high resistance to water, alkali and ageing.

Description

Technical field: [0001] The invention relates to a building material, in particular to a composite exterior wall glass mosaic, a ceramic wall tile veneer surface treatment agent and a production process. Background technique: [0002] The traditional exterior wall veneer ceramic wall is pasted according to the body material and cement. After several years of wind, rain and natural dry and wet climate conditions, some mosaics and tiles will appear cracks, broken and pasted to varying degrees. Parts fall off, seriously affecting the decorative effect of the building and even endangering personal safety. In order to maintain this part of the project well, it is necessary to consider saving money, time and good effect as much as possible. The general method is to re-paste the paint on the surface of the mosaic and the tile. However, due to the interface stress caused by the bonding between the paint and the mosaic and the tile and the difference in the expansion coefficient, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B14/06C04B16/06C04B24/02C04B24/26C04B24/38
Inventor 李淦林
Owner 李淦林