Production of laminated cloth for installing ceramic ball on radial weaving mesh cloth

A technology of mesh cloth and ceramic balls, which is applied in the field of preparation of laminated cloth with ceramic balls installed in diameter-knitted double-layer mesh cloth, can solve the problems such as the lamination method of ceramic balls and fabrics has not been found, and achieve low production costs and high market prospects Good, wide range of effects

Active Publication Date: 2006-08-16
匙馨柱
View PDF1 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, no effective lamination method of ceramic balls and fabrics has been found

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production of laminated cloth for installing ceramic ball on radial weaving mesh cloth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Fill the mesh of the elastic double-layer mesh cloth with ceramic balls, the number of ceramic balls is 30% of the number of mesh;

[0016] The elastic double-layer mesh cloth containing ceramic balls is used as the base layer, the hot-melt fiber cloth is used as the adhesive layer, and the single-layer mesh cloth is used as the surface layer. The three layers are hot-pressed and laminated together; the lamination temperature is 90°C.

Embodiment 2

[0018] Fill the mesh of elastic double-layer nylon mesh cloth with ceramic balls, the number of ceramic balls is 50% of the number of mesh;

[0019] The elastic double-layer nylon mesh cloth containing ceramic balls is used as the base layer, the hot-melt fiber cloth is used as the adhesive layer, and the pure cotton cloth is used as the surface layer, and the three layers are hot-pressed and laminated together; the pure cotton cloth is attached to the elastic double-layer The side of the nylon mesh cloth with ceramic balls is laminated with the base layer under the action of hot-melt fibers. The lamination temperature was 120°C.

[0020] like figure 1 Shown is a schematic diagram of the cross section of the hexagonal elastic nylon mesh cloth. The ceramic balls filled therein have a diameter equivalent to the size of the mesh cloth and can just fill the mesh cloth. The meshes filled with ceramic balls are distributed in a relatively concentrated manner and connected into sh...

Embodiment 3

[0022] Fill ceramic balls in the mesh of elastic nylon spandex mesh cloth, the number of ceramic balls is 80% of the number of mesh;

[0023] The elastic double-layer nylon spandex mesh cloth containing ceramic balls is used as the base layer, the hot-melt fiber cloth is used as the adhesive layer, and the blended cloth is used as the surface layer, and the three layers are hot-pressed and laminated into one; laminated with the double-layer mesh cloth. The lamination temperature was 150°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A laminated cloth used for preparing the health-care far infrared products is prepared through preparing small ceramic balls, filling them in the meshes of warp-knitted dual-layer lace cloth, and combining said dual-layer lace cloth containing small balls, thermofusible fiber cloth as adhesive layer and surficial cloth together.

Description

technical field [0001] The invention relates to a lamination method for installing ceramic balls in diameter-knitted double-layer mesh cloth. technical background [0002] At present, laminated products mostly exist in the form of multilayer boards. Among them, wood, plastic, metal, fabric or a combination thereof are the most common. In the electronics manufacturing industry, there are also some patents disclosing that ceramic powders are fired into ceramic capacitors, such as Chinese patent application 200480001505.4, published on January 4, 2006, and the title of the invention is "ceramic green substrates, laminated ceramic products and their method of preparation". At present, no effective lamination method of ceramic balls and fabrics has been found. Contents of the invention [0003] The present invention overcomes the above-mentioned shortcomings, and proposes an effective lamination method of diameter-knitted double-layer mesh cloth and ceramic balls. [0004] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B37/06B32B37/24B32B5/02B32B18/00
Inventor 匙馨柱陈金泉
Owner 匙馨柱