Method for manufacturing stalk-polystyrene composite thermal-insulated plate

A polystyrene, composite thermal insulation technology, applied in thermal insulation, building components and other directions, can solve the problems of poor energy saving, waste of land resources, destruction of cultivated land, etc., and achieve the effect of light weight and good thermal insulation effect.

Inactive Publication Date: 2006-10-25
SHENYANG JIANZHU UNIVERSITY
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional clay bricks and blocks not only waste a lot of energy in the firing process, but also seriously destroy cultivated land, waste land resources, and the harmful gases and dust emitted will also pollute the environment and bring great harm to people's health
Moreover, its energy-saving effect is relatively poor, so traditional clay bricks and blocks have been banned or restricted in most areas, and energy-saving, green and environmentally friendly building insulation boards will be more and more used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Dry the corn stalks naturally, and add electric heating to dry them, so that the moisture content in the stalks is below 5%, crush the dried corn stalks to a length of 5-10 mm, mix the crushed corn stalks with polystyrene raw materials The particles are mixed according to the mass ratio of 15:1, the mixture is added to the plate mold, and the water vapor at 100°C is passed through the mold to make the polystyrene foam, and the straw and polystyrene particles are adhered to each other to obtain light weight. High-quality building energy-saving insulation board, the thermal conductivity of the insulation board is 0.054W / m 2 K.

Embodiment 2

[0012] Dry the corn stalks naturally, and add electric heating to dry them, so that the moisture content in the stalks is below 5%, crush the dried corn stalks to a length of 5-10 mm, mix the crushed corn stalks with polystyrene raw materials The particles are mixed in a mass ratio of 20:1, the mixture is added to the plate mold, and the water vapor at 100°C is passed through the mold to make the polystyrene foam, and the straw and polystyrene particles are adhered to each other to obtain light weight. High-quality building energy-saving insulation board, the thermal conductivity of the insulation board is 0.071W / m 2 K.

Embodiment 3

[0014] Dry the corn stalks naturally, and add electric heating to dry them, so that the moisture content in the stalks is below 5%, crush the dried corn stalks to a length of 5-10 mm, mix the crushed corn stalks with polystyrene raw materials The particles are mixed in a ratio of 30:1 by mass, and the mixture is added to the plate mold, and the water vapor at 100 ° C is passed through the mold to make the polystyrene foam, and the straw and polystyrene particles are adhered to each other to obtain a light weight. High-quality building energy-saving insulation board, the thermal conductivity of the insulation board is 0.097W / m 2 K.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a manufacture method for stalk-polystyrene compounding warming plate that includes the following steps: insolating the corn stalk, drying to make the water content below 5%, smashing the corn stalk to 5-10mm, mixing with polystyrene raw material according to weight ratio of 15-30:1, adding the mixture into plate mould, adding 100 degree centigrade vapor into mould to make polystyrene foaming, the light construction energy saving plate.

Description

technical field [0001] The invention relates to a preparation method of a building energy-saving material, in particular to a preparation method of a straw-polystyrene composite thermal insulation board. Background technique [0002] With the increasing global energy and resource crisis, people pay more and more attention to building energy conservation. Traditional clay bricks and blocks not only waste a lot of energy in the firing process, but also seriously destroy cultivated land, waste land resources, and the harmful gases and dust emitted will also pollute the environment and bring great harm to people's health. Moreover, its energy-saving effect is relatively poor, so traditional clay bricks and blocks have been banned or restricted in most areas, and energy-saving, green and environmentally friendly building insulation boards will be more and more used. Contents of the invention [0003] The purpose of the present invention is to provide a method for making a buil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08J5/18C08L25/06E04B1/80
Inventor 王博孙驭刘永健
Owner SHENYANG JIANZHU UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap