Method of manufacturing corrosive-resistant single-body hydraulic supporter by salt bath nitriding

A single hydraulic prop, corrosion-resistant technology, applied in metal material coating process, coating, solid-state diffusion coating, etc., can solve problems such as hydrogen embrittlement, coating peeling off, environmental pollution, etc., and achieve fatigue resistance. High, good sealing performance, good anti-corrosion performance

Inactive Publication Date: 2007-03-07
新汶矿业集团通力机械有限责任公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these two methods have the following disadvantages: (1) serious environmental pollution, which is not conducive to physical and mental health, (2) hydrogen embrittlement, which affects the comprehensive mechanical properties of the substrate, (3) there are por

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0014] Example 1:

[0015] A method for manufacturing a corrosion-resistant single hydraulic prop by salt bath nitriding. The method includes the following steps: degreasing, rust removal→alkali washing→cleaning→nitridation salt bath→oxidation salt bath→cooling→cleaning→ Oiled. Specifically:

[0016] (1) The parts that need anti-corrosion treatment on the surface are pretreated by surface degreasing, rust removal, etc., placed in the tooling and fixed, and then placed in an alkaline solution at 75°C for alkaline washing for 5 minutes;

[0017] (2) Put it in a clean water tank at room temperature and wash for 5 minutes;

[0018] (3) Put it into an electric furnace to preheat to 360°C, and put it into a nitriding salt bath in a nitriding furnace;

[0019] (4) Put it into an oxidation salt bath at 440℃;

[0020] (5) After cooling to room temperature, perform the first cleaning at a temperature of 55°C, and perform the second cleaning at a temperature of 80°C;

[0021] (6) Put the oil...

Example Embodiment

[0024] Example 2:

[0025] According to the method described in Example 1: (1) Put it into an electric furnace to preheat to 350°C, and put it into a nitriding furnace in a nitriding salt bath. (2) Put it into an oxidation salt bath at 420℃. (3) After cooling to room temperature, perform the first cleaning at a temperature of 50°C, and perform the second cleaning at a temperature of 75°C. (4) Put the oil in the oil immersion tank at 35℃, and then check the storage.

Example Embodiment

[0026] Example 3:

[0027] According to the method described in Example 1: (1) Put it into an electric furnace to preheat to 340°C, and put it into a nitriding furnace in a nitriding salt bath. (2) Put it into an oxidation salt bath at 430℃. (3) After cooling to room temperature, perform the first cleaning at a temperature of 60°C, and perform the second cleaning at a temperature of 85°C. (4) Put the oil in the oil immersion tank at 40℃, and then check the storage.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a corrosion resistant reinforcing method of disposed component in the salt bath of monomer hydraulic column, which comprises the following steps: removing oil and rust; washing through alkaline; cleaning; nitrogenizing in the salt bath; oxidizing in the salt bath; cooling; cleaning; immersing in the oil.

Description

technical field [0001] The present invention relates to a method for the salt bath nitriding treatment of monolithic hydraulic struts to impart enhanced corrosion resistance to the resulting treated components. Background technique [0002] According to the research and application situation at home and abroad, there are two types of single hydraulic props: internal injection type and external injection type. The external injection type single hydraulic prop is easy to operate, fast, stable in the initial support force, and widely used. Due to the harsh production conditions under the mine, the high air humidity, and the acid and alkaline solution of the mine water, it is easy to make the pillar work together to cause electrochemical corrosion and affect its sealing performance, which cannot meet the requirements for use, and the emulsion is used as the working medium. Single hydraulic props will cause pollution to groundwater resources during use, which is not conducive to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C8/58C23F1/14
Inventor 孙玉祥高文良张正运段秀兰闫秀禄公丕敬王昕王吉庆
Owner 新汶矿业集团通力机械有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap