Microgel-containing composition

a technology of composition and microgel, applied in the field of microgel-containing composition, can solve the problems of inability to prepare tpes, and achieve the effects of improving mechanical properties of composition, improving properties, and dimensional stability and transparency

Inactive Publication Date: 2008-05-08
LANXESS DEUTDCHLAND GMBH +2
View PDF29 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

This approach enables the production of thermoplastic elastomers with customizable properties, improved dimensional stability, transparency, and oil resistance, while avoiding the safety and scalability issues associated with radiation-crosslinked microgels, and allows for the combination of thermodynamically compatible and incompatible polymers.

Problems solved by technology

This is not possible in the TPEs prepared by conventional processes, in which the dispersed phase is formed in situ during the production of the TPEs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microgel-containing composition
  • Microgel-containing composition
  • Microgel-containing composition

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

NBR-Based Microgel from Peroxidic Crosslinking (OBR 1102 C)

[0110] The preparation of the NBR microgel OBR 1102 C was carried out as described in DE 19701487. An NBR latex was used as starting material. The NBR latex had the following features: content of incorporated acrylonitrile: 43 wt. %, solids concentration: 16 wt. %, pH value: 10.8, diameter of the latex particles (dz): 140 nm, particle density: 0.9984 g / cm3, the gel content of the latex is 2.6 wt. %, the swelling index of the gel portion in toluene was 18.5 and the glass transition temperature (Tg) is −15° C.

[0111] 7 phr of dicumyl peroxide (DCP) was used in the preparation of OBR 1102 C.

[0112] Characteristic data of the resulting microgel are summarized in Table 1.

preparation example 2

SBR-Based Microgel from Peroxidic Crosslinking (OBR 1046 C)

[0113] The preparation of the microgel was carried out by crosslinking an SBR latex containing 40 wt. % of incorporated styrene (Krylene 1721 from Bayer France) in latex form with 1.5 phr of dicumyl peroxide (DCP) and subsequently grafting with 5 phr of hydroxyethyl methacrylate (HEMA).

[0114] The crosslinking of Krylene 1721 with dicumyl peroxide was carried out as described in Examples 1) to 4) of U.S. Pat. No. 6,127,488,1.5 phr of dicumyl peroxide being used for the crosslinking. The underlying latex Krylene 1721 has the following features:

solids concentration: 21 wt. %; pH value: 10.4; diameter of the latex

particles: d10=40 nm; dz=53 nm; d80=62 nm; Ospec.=121; particle

density: 0.9673 g / cm3, the gel content of the microgel is 3.8 wt. %, the swelling index of the gel portion is 25.8 and the glass transition temperature (Tg) is −31.5° C.

[0115] After reaction with 1.5 phr of dicumyl peroxide, the product had the foll...

preparation example 3

SBR-Based Microgel from Direct Polymerization; Crosslinking with DVB (OBR1126E)

[0119] The preparation of this microgel was carried out by copolymerization of 23% styrene, 76% butadiene and 1% divinylbenzene in emulsion.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
glass transition temperaturesaaaaaaaaaa
glass transition temperaturesaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a composition containing thermoplastic materials and crosslinked microgels that have not been crosslinked by high-energy radiation, to a process for its preparation, to its use in the production of thermoplastically processable molded articles, and to molded articles produced from the composition.

Description

[0001] This application is a continuation of U.S. patent application Ser. No. 10 / 947,874, filed Sep. 23, 2004, incorporated herein by reference.DESCRIPTION [0002] The present invention relates to a composition containing thermoplastic materials and crosslinked microgels that have not been crosslinked by high-energy radiation, to a process for its preparation, to its use in the production of thermoplastically processable molded articles, and to molded articles produced from the composition. BACKGROUND OF THE INVENTION [0003] The use of microgels for controlling the properties of elastomers is known (e.g. EP-A-405216, DE-A 4220563, GB-PS1078400, DE 19701487, DE 19701489, DE 19701488, DE 19834804, DE 19834803, DE 19834802, DE 19929347, DE 19939865, DE 19942620, DE 19942614, DE 10021070, DE 10038488, DE 10039749, DE 10052287, DE 10056311 and DE 10061174). EP-A-405216, DE-A-4220563 and GB-PS-1078400 disclose the use of CR, BR and NBR microgels in mixtures with double-bond-containing rubb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityApplications(United States)
IPC IPC(8): C08F8/00C08L21/00C08L23/10
CPCC08L21/00C08L23/10C08L2666/02C08L2666/08
InventorHEILIGER, LUDGERFRUH, THOMASMULLER, VOLKERTEBBE, HEIKOOBRECHT, WERNERSCHUSTER, ROBERT HANSMULLER, MARTIN
OwnerLANXESS DEUTDCHLAND GMBH