Aqueous coating composition, process for producing it and two-pack type curable aqueous coating kit

a technology of aqueous coating and composition, which is applied in the direction of coatings, textiles and papermaking, fibre treatment, etc., can solve the problems of reducing the water resistance or weather resistance of the coating film to be obtained, and achieves good dispersion stability, small burden on the environment, and increase the molecular weight of the polymer or gelation

Inactive Publication Date: 2009-09-24
ASAHI GLASS CO LTD
View PDF2 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0017]With respect to the aqueous coating composition of the present invention, the content of an organic solvent is low, whereby a burden on an environment is small, and even if the content of the organic solvent is reduced, increase of the molecular weight of a polymer or gelation is suppressed, whereby the dispersion stability is good, and the storage stability is excellent. Further, the aqueous coating composition of the present invention provides a coating film having good water permeability / water resistance.
[0018]Further, the aqueous coating composition of the present invention provides a two-pack type curable aqueous coating material kit which exhibits the above performances and is easy to be handled.

Problems solved by technology

However, in order to secure the dispersion stability only by an emulsifier, a substantial amount of the emulsifier needs to be used, which causes decrease of the water resistance or weather resistance of a coating film to be obtained.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous coating composition, process for producing it and two-pack type curable aqueous coating kit
  • Aqueous coating composition, process for producing it and two-pack type curable aqueous coating kit
  • Aqueous coating composition, process for producing it and two-pack type curable aqueous coating kit

Examples

Experimental program
Comparison scheme
Effect test

synthesis example 1

[0122]Into a stainless autoclave equipped with a stirrer and having an inner volume of 250 cc (pressure resistance: 50 kg / cm2·G), 10.8 parts of ethyl vinyl ether (EVE), 16.7 parts of cyclohexyl vinyl ether (CHVE), 15.4 parts of ω-hydroxybutyl vinyl ether (HBVE), 4.9 parts of 10-undecenoic acid (UDA), 30 parts of methyl alcohol (MeOH), 37 parts of methyl ethyl ketone (MEK), 0.6 part of tertiary butylperoxypivalate and 0.36 part of dimethylethanolamine (DMAE) were introduced, and dissolved air was removed by deaeration under cooling, whereupon 52.5 parts of chlorotrifluoroethylene (CTFE) was introduced, and a reaction was carried out at 50° C. for 24 hours. After purging and filtration, a varnish of a fluorocopolymer having a solid content of 60.4 mass % was obtained.

[0123]The molecular weight of the fluorocopolymer in the obtained varnish was measured by GPC, and Mn=1.1×104 by a number average as calculated as polystyrene, and the acid value was 15 mgKOH / g.

[0124]By this acid value, i...

synthesis example 2

[0132]An aqueous liquid of Synthesis Example 2 was obtained in the same manner as in Synthesis Example 1 except that the monomer amounts, the solvent amounts, the types and amounts of other additives and the amount of triethylamine used were changed to the amounts shown in is Table 1, 50 mass % of EtOH used as a solvent after the polymerization, was substituted with a solvent, MEK and in distillation of the solvents, the remained solvents were distilled under reduced pressure until their total amount became 15 parts by mass of the solid content of the fluorocopolymer.

synthesis examples 3 , 4 , 6 and 9

Synthesis Examples 3, 4, 6 and 9

[0133]Aqueous liquids of Synthesis Examples 3, 4, 6 and 9 were obtained in the same manner as in Synthesis Example 1 except that the monomer amounts, the solvent amounts, the types and amounts of other additives, and the amount of triethylamine used were changed to the amounts shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
mol %aaaaaaaaaa
mol %aaaaaaaaaa
mol %aaaaaaaaaa
Login to view more

Abstract

To provide an aqueous coating composition which has a low content of an organic solvent, whereby a burden on an environment is small; in which an increase of the molecular weight, gelation, etc. are suppressed; which performs excellent storage stability and provides a coating film having good water permeability/water resistance.
An aqueous coating composition which is a composition obtained by dispersing a fluorocopolymer (A) obtained by a solution polymerization method, in an aqueous medium, and which comprises a repeating unit (1) of fluoroolefin, a repeating unit (2) of a vinyl monomer or an allyl monomer, a repeating unit (3) of a vinyl monomer having a hydroxyl group bonded thereto or of an allyl monomer having a hydroxyl group bonded thereto, and a unit (4) of a vinyl monomer having a carboxylate group bonded thereto or of an allyl monomer, and which comprises a fluorocopolymer (A) wherein a proportion of the repeating unit (4) is from 0.4 mol % to less than 4 mol % based on the total repeating units, and an aqueous medium, wherein an amount of an organic solvent contained in the composition is from 0 to 1 mass %.

Description

TECHNICAL FIELD[0001]The present invention relates to an aqueous coating composition containing a fluorocopolymer containing a carboxylate group, a process for producing it, and a two-pack type curable aqueous coating kit using the aqueous coating composition.BACKGROUND ART[0002]An aqueous coating material is useful as a coating material suitable for natural environmental protection since it is possible to reduce the content of an organic solvent as compared with a solvent type coating material. As a process for producing the aqueous coating material, a process to obtain a water-dispersion by emulsion polymerization of a fluorocopolymer, is known. However, in order to secure the dispersion stability only by an emulsifier, a substantial amount of the emulsifier needs to be used, which causes decrease of the water resistance or weather resistance of a coating film to be obtained. As one of the methods to solve such a problem, it has been proposed to introduce hydrophilic moieties in a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(United States)
IPC IPC(8): C09D127/12
CPCC09D127/12C09D123/00
Inventor SUMI, NAOKOMORIZUMI, TAKASHIKIMURA, ISAO
Owner ASAHI GLASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap