Composite impactor for percussion crushers

a technology of percussion crusher and composite material, which is applied in the field of composite material impactor for percussion crusher, can solve the problems of not revealing a reinforcement structure and a durable bond

Active Publication Date: 2011-09-22
MAGOTTEAUX INT SA
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0012]The present invention discloses a composite impactor for percussion crushers, said impactor comprising a ferrous alloy reinforced at least partially with titanium carbide according to a defined geometry, in which said reinforced portion comprises an alternating macro-microstructure of millimetric areas concentrated with micrometric glob...

Problems solved by technology

However it does not disclose a reinforcement structure with spheroidal particles of titanium carbide surrounded by the infiltration alloy or any hierarchized microscopic geometry in the reinforced portion.
The common p...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite impactor for percussion crushers
  • Composite impactor for percussion crushers
  • Composite impactor for percussion crushers

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0092]In this example, the aim is to make an impactor, the reinforced areas of which comprise a global volume percentage of TiC of about 42%. For this purpose, a strip is made by compaction to 85% of the theoretical density of a mixture of C and of Ti. After crushing, the granules are sifted so as to obtain a dimension of granules located between 1.4 and 4 mm. A bulk density of the order of 2.1 g / cm3 is obtained (35% of space between the granules+15% of porosity in the granules).

[0093]The granules are positioned in the mold at the location of the portion to be reinforced which thus comprises 65% by volume of porous granules. A cast iron with chromium (3% C, 25% Cr) is then cast at about 1500° C. in a non-preheated sand mold. The reaction between the Ti and the C is initiated by the heat of the cast iron. This casting is carried out without any protective atmosphere. After reaction, in the reinforced portion, 65% by volume of areas with a high concentration of about 65% of globular t...

example 2

[0094]In this example, the aim is to make an impactor, the reinforced areas of which comprise a global volume percentage of TiC of about 30%. For this purpose, a strip is made by compaction to 70% of the theoretical density of a mixture of C and of Ti. After crushing, the granules are sifted so as to obtain a dimension of granules located between 1.4 and 4 mm. A bulk density of the order of 1.4 g / cm3 is obtained (45% of space between the granules+30% of porosity in the granules). The granules are positioned in the portion to be reinforced which thus comprises 55% by volume of porous granules. After reaction, in the reinforced portion, 55% by volume of areas with a high concentration of about 53% of globular titanium carbide are obtained, i.e. about 30% by the global volume of TiC in the reinforced portion of the impactor.

example 3

[0095]In this example, the aim is to make an impactor, the reinforced areas of which comprise a global volume percentage of TiC of about 20%. For this purpose, a strip is made by compaction to 60% of the theoretical density of a mixture of C and of Ti. After crushing, the granules are sifted so as to obtain a dimension of granules located between 1 and 6 mm. A bulk density of the order of 1.0 g / cm3 is obtained (55% of space between the granules+40% of porosity in the granules). The granules are positioned in the portion to be reinforced which thus comprises 45% by volume of porous granules. After reaction, in the reinforced portion, 45% by volume of areas concentrated to about 45% of globular titanium carbide are obtained, i.e. 20% of the global volume of TiC in the reinforced portion of the impactor.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Lengthaaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

The present invention discloses a composite impactor for percussion crushers, said impactor comprising a ferrous alloy at least partially reinforced with titanium carbide according to a defined geometry, in which said reinforced portion comprises an alternating macro-microstructure of millimetric areas concentrated with micrometric globular particles of titanium carbide separated by millimetric areas essentially free of micrometric globular particles of titanium carbide, said areas concentrated with micrometric globular particles of titanium carbide forming a microstructure in which the micrometric interstices between said globular particles are also filled by said ferrous alloy.

Description

FIELD OF THE INVENTION[0001]The present invention relates to a composite impactor for percussion crushers, percussion crushers grouping machines for crushing rocks and hard materials such as crushers with hammers, bar crushers, crushers with a vertical axis etc. These machines are extensively used in the first and second steps of a manufacturing line intended to drastically reduce the rock size in extractive industries (mines, quarries, cement works, . . . ) and recycling industries.DEFINITION[0002]The expression “impactor for percussion crushers” should be interpreted in a broad sense, i.e. a composite wear part which has the function of being in direct contact with the rock or the material to be milled during the phase of the method when these rocks and materials are subject to extremely violent impacts intended to fragment them.These wear parts therefore show a great resistance to impact and they are often called hammers, bars or impactors. The term “impactor” therefore encompass...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B02C13/28B22D19/14
CPCB02C13/28B22D19/14B22D19/06B02C2210/02
Inventor BERTON, GUY
Owner MAGOTTEAUX INT SA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap