Production of crystal jade glass

A production method and glass technology, applied in glass forming, glass reshaping, glass manufacturing equipment, etc., can solve problems such as low yield, high requirements for glass powder, affecting the smoothness of the surface glass layer, etc., and achieve stable internal quality , stable quality, and the effect of eliminating air bubbles

Inactive Publication Date: 2007-11-14
邱文正 +3
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the two methods of making crystal jade glass described above all need to use powdered glass in the production process, so the production requirements are very strict. If the glass powder falls to the surface before the surface glass layer is made The bottom of the flat glass used to make the surface glass layer will not only affect the smoothness of the finished surface glass layer, but also has high requirements for glass powder. A little impurity will make the product easy to burst and the internal quality is difficult. Control, yield rate is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production of crystal jade glass
  • Production of crystal jade glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] With reference to Fig. 1, Fig. 2, Fig. 3, Fig. 4, a kind of manufacturing method of crystal jade glass, its steps are as follows:

[0019] (a) making the mold 5' with concrete or abstract concave and convex surfaces at the bottom, the mold 5' can be a high-temperature pottery mold or other high-temperature-resistant material mould;

[0020] (b) Put mold release agent 7' on the mold 5' bottom described in step (a), place the plate glass 1' with color layer 3' on the upper surface in the mold 5', and then place another plate glass 2 'placed above the plate glass 1' with the color layer 3', and the bottom surface of the above plate glass 2' is coated with a low-temperature flux 4'. Wherein, the flat glass with the color layer and the flat glass coated with the low-temperature flux can adopt ordinary glass plates with a softening point of about 550-700°C; A flux with a low softening point of the plate, such as a flux below 500°C, can advance the softening point of the glas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
Login to View More

Abstract

Production of crystal glass is carried out by overlaying two glass plates together, baking and coating low-temperature fluxing agent. It can prevent powdery glass from dropping, lower softening point and eliminate bubble. It has better yield and quality.

Description

technical field [0001] The invention relates to a method for making crystal jade glass made of flat glass and having excellent decorative effect. Background technique [0002] With the development of modern society, the demand for high-grade decorative materials is increasing, and the requirements are getting higher and higher. Traditional decorative materials such as marble and granite have disadvantages such as poor corrosion resistance, poor weathering resistance, and easy wear and tear, so they are not suitable for interior and exterior wall decoration materials. Although ordinary ceramics are rich in color and many styles, they are widely used in various places, but they are not very hard and easy to wear, and the color material attached to the surface is easy to fall off, and the pattern is easy to be scratched, which requires certain maintenance. In addition, recently there is a kind of glass-ceramic decorative brick, which has high hardness, wear resistance, and is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03B23/02C03B23/203C03C1/00
Inventor 邱文正
Owner 邱文正