Production of nanometer heater for tumor magnetic thermal therapy

An exothermic agent and magnetotropic technology, applied in cooling appliances for treatment, heat exchange materials, chemical instruments and methods, etc., can solve problems such as not paying attention to the volume of the reaction system, and reduce the difficulty and cost of equipment manufacturing , less investment in equipment, and the effect of improving the heating effect

Inactive Publication Date: 2008-03-05
SOUTHEAST UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, judging from the current research situation at home and abroad, the wet chemical co-precipitation method at room temperature can generally only obtain iron oxide particles smaller than 20nm, probably because the reaction system they use is small and the influence of the volume of the reaction system is not noticed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production of nanometer heater for tumor magnetic thermal therapy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] step 1):

[0025] Preparation of Fe by wet chemical co-precipitation method 3 o 4 Nanoparticles, the reaction is carried out in a 1-liter beaker or a 5-liter beaker or a 50-liter high-speed stirring reactor, and the reaction raw material is FeCl 3 and FeSO 4 Press Fe3+ / Fe 2+ = Mix at a certain ratio between 1.4-1.7 and add to a beaker or reactor, under stirring conditions, add 2.5% ammonia solution into the beaker or reactor through the addition funnel to chemically react with iron salt until pH = 9, stop adding Ammonia, continue to stir for 1 h and then stop the reaction, and protect the whole reaction process with nitrogen gas.

[0026] Step (2):

[0027] Prepared Fe 3 o 4 Nanoparticles, after washing 3-4 times by magnetic separation, diluted with water to 2-4 g / l water-based Fe 3 o 4 The magnetic liquid is then oxidized with air at 90-100°C, pH = 2-3, and stirred for 4-5 hours to form a water-based γ-Fe 2 o 3 magnetic fluid.

[0028] Step (3):

[0029] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

Production of heating agent for tumor magnetic thermal therapy is carried out by preparing Fe3O4 nanometer particles from wetting chemical coprecipitation, regulating reactant proportion and increasing volume of reacting system to regulate size of Fe3O4 nanometer particles, washing reactant for 3-4 times from magnetic separation, diluting to 2-4g / lwater based Fe3O4 magnetic liquid from water, stirring at 90-100 DEG C and pH=2-3, inducing into air, oxidizing for 4-5hrs, forming water based gamma-Fe3O4 magnetic liquid, cooling, adding into glutamic acid 5-10wt%, surface modifying, keeping pH=3+-0.1 and stirring for 4-5hrs, washing for 3-4 times from magnetic separation, obtaining stabilized nanometer heating agent, and dissolving into different concentration 0-20g / l.

Description

technical field [0001] The invention relates to a preparation method of a functional material used for tumor magnetic hyperthermia, and belongs to the technical field of biological and medical nanometer material production. Background technique [0002] Magnetothermal therapy is a promising tumor treatment method under development. It achieves the therapeutic purpose by means of the heating effect of the magnetic material (heating agent) distributed in the tumor tissue in an external alternating magnetic field. kind of. It is generally required that the magnetic material can convert the energy of an external alternating magnetic field to raise the temperature of the tumor tissue to 42-47°C, thereby killing tumor cells. Nanomagnetic particles are easy to disperse and administer, and absorb more magnetic field energy than micron or larger-sized microspheres, which can reduce the requirement for the output power of an external alternating magnetic field, or reduce the dosage, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K5/10A61F7/03
Inventor 顾宁张宇马明
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com