Mosaic and processing method thereof

A mosaic, heating temperature technology, applied in the field of building decoration materials and their processing, can solve the problem of mosaic decoration effect is not strong, to achieve a strong decorative effect

Inactive Publication Date: 2008-12-03
成都再建装饰材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to overcome the deficiency that the existing mosaic has a weak decorative effect during use, the technical problem to be solved by the present invention is to provide a mosaic with a strong decorative effect and its processing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1: the mosaic of the present invention selects compact volcanic rock as the body material to make the body, the glaze body adopts opaque raw material glaze, and then adopts the following process steps to make the mosaic with cracks of the present invention:

[0021] (1) After heating the volcanic rock body to 50°C, apply a surface glaze with a fineness of 120 mesh and a dry glaze with a particle size of 20 mesh to form a biscuit body covered with glaze;

[0022] (2) heating the above-mentioned biscuit blank to a firing temperature of 800° C. for 30 to 50 minutes, and keeping it warm for 4 to 8 minutes;

[0023] (3) Take out of the oven and cool naturally.

Embodiment 2

[0024] Embodiment 2: For the mosaic of the present invention, porous volcanic rock with a pore diameter of 0.2-1 mm is selected as the body material, and transparent frit glaze is selected for the glaze body. The green body is made of volcanic rock material, and then the mosaic with cracks of the present invention is made by the following process steps:

[0025] (1) After heating the volcanic rock body to a heating temperature of 80°C, apply a make-up soil primer, then heat it to a firing temperature of 900°C for 30 to 50 minutes, keep it warm for 4 to 8 minutes, and then release it from the furnace;

[0026] (2) When cooling to 100°C, apply a surface glaze with a fineness of 250 mesh and a dry glaze with a granularity of 60 mesh to form a biscuit body covered with glaze;

[0027] (3) heating the above-mentioned biscuit blank to a firing temperature of 1100° C. for 30 to 50 minutes, and keeping it warm for 4 to 8 minutes;

[0028] (3) Take out of the oven and cool naturally. ...

Embodiment 3

[0029] Embodiment 3: For the mosaic of the present invention, the porous volcanic rock of 0.2-1 mm is selected as the body material to make the body, and the glaze body is made of transparent frit glaze. Then adopt the following processing steps to make the mosaic with cracks of the present invention:

[0030] (1) After heating the volcanic rock body to a heating temperature of 100°C, apply a make-up soil primer, and then heat it to a firing temperature of 1100°C for 30 to 50 minutes, keep it warm for 4 to 8 minutes, and then release it from the furnace;

[0031] (2) When cooling to 80°C, apply a surface glaze with a fineness of 150 mesh and a dry glaze with a particle size of 40 mesh to form a biscuit body covered with glaze;

[0032] (3) heating the above-mentioned biscuit blank to a firing temperature of 1100° C. for 30 to 50 minutes, and keeping it warm for 4 to 8 minutes;

[0033] (3) When the glaze is cooled to 50-100°C, apply gold water or silver water decorative glaze...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a mosaic and manufacturing method, which consists of mould and glazer, wherein the mould is volcanic rock; the irregular crack is displayed on the whole grazing surface. The manufacturing method comprises the following steps: heating mould; coating glazer; sintering.

Description

[0001] (This application is a divisional application of the application with the application number 200410081201.5, the application date is November 9, 2004, and the invention name is ceramic tile, mosaic and its processing method) technical field [0002] The invention relates to a building decoration material and a processing method thereof, especially a mosaic and a processing method thereof. Background technique [0003] At present, the existing ceramic tiles and mosaics are made of body and glaze together. The raw materials used in the body-matrix are mainly clay, feldspar, quartz, etc., which have good strength, Water absorption and firing performance, etc. Its production process generally goes through: raw material pulping - raw material powder milling - powder molding - glazing - firing completion and other technological steps. Specifically, the raw material is ground into a certain fineness slurry by a ball mill, and the slurry is made into a certain particle size ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/34
Inventor 黄永建
Owner 成都再建装饰材料有限公司