Preparation method of nickel-hydrogen battery

A nickel-metal hydride battery, conductive graphite technology, applied in battery electrodes, alkaline battery electrodes, secondary battery charging/discharging, etc., can solve the problems of low life, low battery capacity, and soaring battery production costs, and reduce production. cost, cost reduction effect

Inactive Publication Date: 2009-12-30
邹平铭波电源有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Due to the rapid rise in the price of nickel, the main raw material of the positive electrode, the production cost of the battery has increased sharply. In order to reduce the cost, the nickel electrode can no longer be used.
The current substitute electrodes include: double-sided burr steel strip, cable-drawn mesh steel strip, flat punched steel strip, etc. However, the current substitute technology has the following shortcomings: the battery capacity is low, the life is low, and the self-discharge is too large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The technological process that realizes the object of the present invention is:

[0012] Combining powder→pulping→pulling sheet→finishing→winding→assembly→chemical formation→capacity inspection→life test.

[0013] A kind of preparation method of nickel-metal hydride battery, first prepare positive electrode according to the following method:

[0014] First, the active material is added to a certain amount of additives containing conductive short fibers and conductive graphite, and the addition amounts are: Ni(OH) 2 86 parts by weight, CaCO 3 1 parts by weight, CoO13 parts by weight, additives 2 parts by weight.

[0015] Add the mixture of sec-butyl acetate (SBA) and styrene-butadiene rubber (SBR) after mixing the powder to make adhesive slurry, and the addition of sec-butyl acetate (SBA) and styrene-butadiene rubber (SBR) is 10 parts by weight respectively number.

[0016] Then the slurry is hung on the three-dimensional steel belt through continuous drawing, and a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention relates to a positive of a NiH cell taking steel ribbon as a matrix, which is taken to be the positive replacing foam Ni material so as to reduce production cost including the following steps: a positive of a NiH cell with a steel ribbon as its matrix, and the surface of the steel ribbon is coated with additive containing conducting short fiber and conductive graphite by a pulping technology.

Description

technical field [0001] The invention relates to the field of batteries, in particular to a method for preparing a nickel-metal hydride battery. Background technique [0002] Due to the rapid increase in the price of nickel, the main raw material of the positive electrode, the production cost of the battery has increased sharply. In order to reduce the cost, the nickel electrode can no longer be used. The current substitute electrodes include: double-sided burr steel strip, cable-drawn mesh steel strip, flat punched steel strip, etc. However, the current substitute technology has the following shortcomings: the battery capacity is low, the life is low, and the self-discharge is too large . Contents of the invention [0003] In order to overcome the above disadvantages, the present invention proposes a method for preparing a nickel-metal hydride battery, which uses a steel strip as the substrate and replaces the foamed nickel material as the positive electrode, so as to gre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/24H01M4/62H01M4/52H01M4/26H01M10/44H01M4/64
CPCY02E60/124Y02E60/10
Inventor 李信
Owner 邹平铭波电源有限公司