Epoxy anti-rust paint capable of thick-film coating and saitable for construction in winter and preparing method

An anti-rust paint and environmental technology, applied in the direction of epoxy resin coating, coating, anti-corrosion coating, etc., can solve the problems of thick film construction, limited use, construction difficulty, etc., to reduce the construction period, save energy, and process methods Simple and convenient effect

Inactive Publication Date: 2007-11-14
上海华谊精细化工有限公司上海开林造漆厂
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, because the traditional epoxy antirust paint is cured and cross-linked at room temperature to form a film, it must be applied at an ambient temperature above 5°C. In addition, it cannot be applied with a thick film, otherwise it will cause problems with the paint film
For example, using the traditional epoxy antirust paint on the market, the curing reaction will stop after construction below 5°C, thus causing various defects of the paint film; in addition, the traditional epoxy antirust paint generally sprays more than 300μm will cause sag problem
These defects have brought great difficulties to the construction, and also limited the use of epoxy antirust paint with good anticorrosion performance on large steel structures.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Add 60kg of E-44 resin, 20kg of toluene, and 20kg of isopropanol into the reaction pot and heat and stir until uniform. The temperature is controlled at 50°C to make it a uniform transparent liquid, and the solid content is 60%. Step 3: Add 30kg of E-44 resin liquid, 50kg of gray cloud iron, 8kg of talc, and 3kg of AT-U additives into the high-speed adjustment cylinder and stir for 30 minutes to make it a uniform liquid. Add 3kg of toluene and isopropanol 2kg is qualified when the twist is adjusted to 1.5 Poises, and it is filtered and packaged with 80 mesh sieve as component A.

[0039] Mix 30kg of NX-2015, 5kg of NX-2040, 10kg of NX-2041, 15kg of talc, 7kg of toluene, and 8kg of isopropanol, and add them into the mixing tank and stir for 30 minutes to make it a uniform liquid, then use 80 The mesh filter is packaged as part B, and when used, mix and stir evenly according to the weight ratio of 5:1, and use it up within 2 hours.

[0040] The method specified in the GB...

Embodiment 2

[0042] Add 60kg of E-20 resin, 20kg of toluene, and 20kg of isopropanol into the reaction pot and heat and stir until uniform. The temperature is controlled at 80°C to make it a uniform transparent liquid, and the solid content is 60%.

[0043] Add 30kg of E-20 resin liquid, 50kg of gray cloud iron, 8kg of talc, and 3kg of AT-U additives into the high-speed adjustment cylinder and stir for 30 minutes to make it a uniform liquid. Add 3kg of toluene and 2kg of isopropanol to adjust the temperature. Degree to 1.5Poises is qualified, with 80 mesh sieve filter packaging as component A.

[0044] Mix 30kg of NX-2015, 5kg of NX-2040, 10kg of NX-2041, 15kg of talc, 7kg of toluene, and 8kg of isopropanol, and add them into the mixing tank and stir for 30 minutes to make it a uniform liquid, then use 80 The mesh filter is packaged as part B, and when used, mix and stir evenly according to the weight ratio of 10:1, and use it up within 2 hours.

[0045] The method specified in the GB9264...

Embodiment 3

[0047] Add 60kg of E-42 resin, 20kg of toluene, and 20kg of isopropanol into the reaction pot and heat and stir until uniform. The temperature is controlled at 65°C to make it a uniform transparent liquid, and the solid content is 60%. Step 3: Add 30kg of E-42 resin liquid, 50kg of gray cloud iron, 8kg of talc, and 3kg of AT-U additives into the tank and stir for 30 minutes to make it a uniform liquid. Add 3kg of toluene and 2kg of isopropanol Adjust the twist to 1.5 Poises to be qualified, filter and pack with 80 mesh sieve as component A.

[0048] Mix 30kg of NX-2015, 5kg of NX-2040, 10kg of NX-2041, 15kg of talc, 7kg of toluene, and 8kg of isopropanol, and add them into the mixing tank and stir for 30 minutes to make it a uniform liquid, then use 80 The mesh filter is packaged as part B, and when used, mix and stir according to the weight ratio of 7.5:1, and use it up within 2 hours.

[0049]The method specified in the GB9264-88 standard was used to test, and the results a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

This invention relates to one kind of epoxy antirust paints, discloses one kind of epoxy antirust paints and its making method that can spray by using the thick film and construct under the winter environment. This invention begins with ameliorating the model material, selects the modified amines firming agent and the epoxy group to response, and add preventing flowing hang-aid material, when using the epoxy antirust paint of this invention to paint, not being restricted because the temperature is lower than 5 degree C. In addition, it can do a construction of one-time thick film spray, the wet film thickness can achieve 600 mu m, after uniformly mixing the Group A and B, it has excellent film-forming character and good storage stability under the normal or low temperature (above -10 degree ).

Description

technical field [0001] The invention relates to an epoxy antirust paint, in particular to an epoxy antirust paint capable of thick-film spraying and suitable for construction in winter environments and a preparation method thereof. Background technique [0002] With the continuous development of the national economy and basic construction, national key projects and large-scale projects have higher and higher requirements for anti-corrosion. Large-scale steel equipment and components have higher requirements for coatings, which require coatings to have excellent anti-corrosion properties. Performance, but also must have good construction and adaptability. Epoxy antirust paints are known to have good chemical and corrosion resistance. [0003] However, since the traditional epoxy antirust paint is cured and cross-linked at room temperature to form a film, it must be applied at an ambient temperature above 5°C. In addition, it cannot be applied with a thick film, otherwise it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/08
Inventor 许莉莉李华刚毛晨峰杜伟娜
Owner 上海华谊精细化工有限公司上海开林造漆厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap