Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Production of composite waterproof hung-laying curling material of self-adhesive and high-strength rubber

A production method and self-adhesive technology, which is applied to rubber layered products, chemical instruments and methods, and other chemical processes, can solve the problems of adhesive pollution, use restrictions, and inability to construct, and achieve large elongation and improved Composite strength, good affinity effect

Inactive Publication Date: 2007-11-21
天津市腾祥科技发展有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the rubber coil is bonded to the base surface of the structure, the bonding condition requires that the moisture content of the base surface be less than or equal to 8%, otherwise the construction cannot be carried out, and the use is limited; moreover, the adhesive also pollutes the environment and has high costs. ills

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Take the production method of the high-strength self-adhesive rubber composite waterproof hanging pavement coil used in the waterproof project of the underground railway as an example

[0031] I. Preparation of Non-Vulcanized Rubber Sheets

[0032] ingredients

[0033] Based on synthetic rubber, prepare raw materials according to the following weight ratio

[0034] Synthetic Rubber - Butyl Rubber 100

[0035] Tackifier - Polyisobutylene 10

[0036] Accelerator-M 1.2

[0037] Hydrophilic agent - sodium oleate 3.2

[0038] Wherein, accelerator M is thiol benzothiazole.

[0039] The above materials are heated and kneaded at a temperature of 80°C, then parked for 24 hours, re-milled at a temperature of 60-70°C for 20 minutes, calendered or extruded into sheets.

[0040] II. Preparation of Unvulcanized Vulcanized Rubber Sheets

[0041] ingredients

[0042] Based on synthetic rubber, prepare raw materials according to the following weight ratio

[0043] Synthetic Rub...

Embodiment 2

[0060] Take the production method of the high-strength self-adhesive rubber composite waterproof hanging pavement roll for bridge and tunnel waterproofing engineering as an example

[0061] I. Preparation of Non-Vulcanized Rubber Sheets

[0062] ingredients

[0063] Based on synthetic rubber, prepare raw materials according to the following weight ratio

[0064] Synthetic Rubber - Butyl Rubber 100

[0065] Tackifier - Polyisobutylene 9

[0066]Accelerator-D 1.2

[0067] Hydrophilic agent - sodium oleate 3.2

[0068] The preparation method is the same as in Example 1.

[0069] II. Preparation of Unvulcanized Vulcanized Rubber Sheets

[0070] ingredients

[0071] Based on synthetic rubber, prepare raw materials according to the following weight ratio

[0072] Synthetic Rubber - EPDM 100

[0073] Vulcanizing agent-S 1.5

[0074] Accelerator-TT 0.8

[0075] Active agent - ZnO 5

[0076] Wherein, the accelerator TT is tetramethylthiuram disulfide.

[0077] The preparat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strength at breakaaaaaaaaaa
tensile strength at breakaaaaaaaaaa
Login to View More

Abstract

Production of high-strength self-adhesive hung and spreading coiling material of composite water-proof rubber is carried out by preparing non-vulcanized rubber sheet, synthesizing rubber 100, tack producing agent-polyisobutylene 8-10, improver 1.0-1.6 and hydrophilic agent-sodium oleate 2-5 proportionally, cooking, milling, laying aside for 24 hrs, calendaring or extruding into slices, preparing un-vulcanized rubber sheet, synthesizing rubber 100, activator 2.5-5, vulcanizing agent-S1-5 and improver 2-4 proportionally, milling, laying aside for 24 hrs, cooking at 70-80 degree, forming by calendaring stack or extruder, combining, and passing non-woven fabric sheet, vulcanized rubber sheet and non-vulcanized rubber sheet through vulcanizing drum successively to obtain final product. The products consist of non-woven fabric layer, vulcanized rubber layer and non-vulcanized rubber layer. It has better affinity with concrete, penetration resistance and extendibility and no leakage. It can be used for water proofing layer of underground architecture.

Description

Technical field: [0001] The invention relates to a manufacturing method of a waterproof component used for the waterproof layer of underground structures. In particular, the invention relates to a manufacturing method of a high-strength self-adhesive rubber composite waterproof hanging paving coil. Background technique: [0002] Underground structures must be provided with a waterproof layer due to the impact of the groundwater level. For the waterproof layer of the vertical wall, its bottom surface needs to have affinity with the wet base of the structure, and its upper surface must have a firm bond with the concrete; in addition, the waterproof layer must also withstand vibration and extrusion, and must have a certain Strength of. [0003] At present, rubber coils are often used as waterproof components for the waterproof layer of underground structures. During construction, the rubber coils are bonded to the base surface of the structure to form a waterproof layer. How...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/18B32B25/10C08L21/00
Inventor 郑宏祥张子宏刘新酉杨涵
Owner 天津市腾祥科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com