Ordered meso-porous silicon oxide and rapid preparation method thereof

A mesoporous silicon oxide, fast technology, applied in the directions of silicon oxide, silicon dioxide, etc., can solve the problems of the preparation operation of propagating materials, increase the preparation cost, etc., and achieve a fast and simple preparation method, good removal ability, and hydrothermal stability. Good results

Inactive Publication Date: 2007-12-05
NANJING UNIV OF SCI & TECH
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the problem with this method is that the drying process needs to use a vacuum environment to remove the TMOS hydrolyzate met

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ordered meso-porous silicon oxide and rapid preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The rapid preparation method of the ordered mesoporous silica of the present invention adopts the direct template method, with the high-concentration solution of the tri-block copolymer P123 as the template, and tetraethyl orthosilicate (TEOS) as the silicon source. quickly in the system. The final material molar ratio is TEOS:P123:HCl=1:0.0367:0.0038. The present invention will be described in further detail below in conjunction with the accompanying drawings.

[0018] In actual operation, the required amount of mesoporous silica can be prepared by fixing the ratio of materials and changing the amount of reactants. Taking the preparation of a 7.9g sample as an example, the specific operation steps are:

[0019] (1) Accurately weigh 14g of P123 into a three-necked flask, add 30mLTEOS, and stir in a 60°C water bath until completely dissolved;

[0020] (2) Add 10mL of 0.05mol / L hydrochloric acid solution rapidly to the reaction solution, stir rapidly to form a thick pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses ordered mesoporous silica and its fast preparation process in an acid system with high concentration solution of three block copolymer P123 as the template agent and ethyl silicate (TEOS) as silicon source. The ordered mesoporous silica has the features of high degree of order, complete spatial group structure, great pore size, thick pore wall and high hydrothermal stability. Its preparation process is simple, fast, easy in operation, environment friendly and low in cost. It may be post-treated properly to prepare excellent adsorbent as one kind of environment protecting material or inorganic separating film with high flux, high selectivity and broad application range.

Description

a technical field [0001] The invention belongs to the field of ordered mesoporous materials, and in particular relates to an ordered mesoporous silicon oxide with a large-aperture three-dimensional bicontinuous pore structure and a rapid preparation method thereof. Two background technology [0002] Ordered mesoporous materials have the advantages of high specific surface area, narrow pore size distribution, continuously adjustable pore size within a certain range, and easy surface modification. It has great application potential in the fields of separation and catalysis. With the deepening of research on mesoporous materials, different types of mesoporous materials have been reported one after another, among which the space group is The ordered mesoporous silica has a helical double continuous cubic structure. This structure is characterized by two sets of three-dimensional channels that are identical but not connected to each other. They have high symmetry and good conne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B33/18
Inventor 李健生王连军郝艳霞苗小郁孙秀云刘晓东
Owner NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap