Metal corsslinking molecular film-forming bi-component water carpentry paint and preparation method thereof

A water-based wood lacquer and metal cross-linking technology, which can be applied to coatings, devices for coating liquid on surfaces, etc., can solve the problems of difficulty in promotion, high cost, and difficulty in obtaining raw materials, and achieves transparent and uniform appearance, excellent stability, The effect of good hardness

Active Publication Date: 2010-12-22
GUANGDONG HUALONG COATING IND
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The two-component water-based paints that have been developed at present mainly include two-component water-based polyurethane (PU) and two-component water-based epoxy two major categories of products, but both are difficult to popularize. The first reason is that the cost is high and the raw materials are difficult to obtain; the reason The second is that the construction is very inconvenient. The curing agent itself is oily, and it needs to be added to the water-based system to emulsify and disperse to react well. Therefore, in order to achieve complete dispersion and uniformity, special measuring and stirring equipment is often required, which brings great benefits to its practical application. Inconvenience
[0005] At present, there is no report on the application of metal crosslinking technology to two-component water-based wood coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal corsslinking molecular film-forming bi-component water carpentry paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0082] Embodiment one, the preparation of bright varnish

[0083] 1. Main paint A component:

[0084] (1) Synthesis of water-soluble water-based resin I:

[0085] Table 1 Water-based resin I formula table

[0086] Composition

[0087] 12 parts of unsaturated monomer butyl acrylate, 30 parts of methyl methacrylate and 18 parts of carboxylic acid-containing monomer acrylic acid are carried out solution polymerization in the cosolvent ethylene glycol butyl ether according to the proportioning in Table 1, and the ethylenic monomer obtained The bulk copolymer solution was distilled under reduced pressure to remove low-molecular substances, then neutralized with 10 parts of ammonia water, and added 10 parts of deionized water to obtain completely water-soluble water-based resin I.

[0088] (2) Preparation of main paint:

[0089] The composition of table 2 main paint

[0090] recipe ingredients

[0091] Add water-soluble water-based resin I into the container...

Embodiment 2

[0101] Embodiment two, the preparation of matte varnish

[0102] 1. Main paint A component:

[0103] (1) Preparation of water-soluble water-based resin II

[0104] Table 5 Water-based resin II formula table

[0105] Composition

parts by weight

Decyl acrylate

10.0

Styrene

22.0

Methacrylate

8.0

Cyclohexanone

10.5

Ethylenediamine

5.5

distilled water

44.0

[0106] According to the ratio in Table 5, 10 parts of unsaturated monomer decyl acrylate, 22 parts of styrene and 8 parts of carboxylic acid monomer methacrylic acid are solution polymerized in the cosolvent cyclohexanone to obtain the ethylenic monomer copolymer The solution was distilled under reduced pressure to remove low-molecular substances, then neutralized with 5.5 parts of ethylenediamine, and added 44 parts of distilled water to obtain completely water-soluble water-based resin II.

[0107] (2) Preparation of main paint:

[010...

Embodiment 3

[0119] Embodiment three, the preparation of colored paint:

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a metal cross linking molecular film formation and two-component waterborne wood lacquer and a preparation method thereof. The waterborne wood lacquer consists of a component A and a component B; the component A is the main paint, consisting of components with the weight portion of water-soluble waterborne additive of 55 to 98 shares, waterborne additive of 0.5 to 10 shares, film forming additive of 0 to 13 shares, pigment or filling of 0 to 44 shares; the component B consists of cross linking agent containing multivalent metal ions. The preparation method consists of the steps: 1. water soluble waterborne resin is prepared; 2. the main paint of component A are prepared; 3. the main paint of component A and the cross linking agent of component B are mixed, so as to obtain the waterborne wood lacquer. The preparation method of the invention is simple and convenient, the formulation cost and the production cost are lower, and the main raw material is stable in price and readily available. The film hardness, fullness, anti-high temperature back viscous, water resistance, grind ability, drying capacity, etc. of the obtained product are improved greatly, the costof production is lowered and the T toleration of construction and the maneuverability are improved. The external condition is also characterizes by solvent woodenware coating.

Description

technical field [0001] The invention relates to the technical field of chemistry and chemical engineering, in particular to a water-based wood varnish and a preparation method thereof. technical background [0002] As a class of important surface beautification and protection decoration materials, wood lacquers are widely used in people's lives. However, traditional wood paints are basically solvent-based paints, such as polyurethane paints, nitro paints, alkyd paints, etc., which contain a large amount of volatile organic solvents, which will produce many toxic and irritating substances during the production and use of paints. Some organic compounds also contain strong carcinogens such as benzene, formaldehyde, and free TDI, which have caused serious harm to people's health and the surrounding environment. [0003] With the development of the society, the prosperity of the economy and the improvement of living standards, people are more concerned about their own health, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B05D7/06C09D201/02
Inventor 罗爱民
Owner GUANGDONG HUALONG COATING IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products