Method for preparing heat-resisting modified polypropylene resin with high glossiness

A polypropylene resin, heat-resistant modification technology, applied in the field of polypropylene resin manufacturing, can solve problems such as general lubricant performance

Active Publication Date: 2008-06-04
SINOPEC SHANGHAI PETROCHEMICAL CO LTD
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In terms of improving the gloss of the product, the performance of these existing lubricants is relatively general.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～10

[0028] The additives used in each embodiment include:

[0029] Nucleating agent A: 2,2-methylene-bis(4,6-di-tert-butylphenoxy)sodium phosphate;

[0030] Nucleating agent B: 3MgO 2 4SiO2 2 ·H 2 O;

[0031] Lubricant: Glyceryl Monopalmitate;

[0032] Antioxidant A: tetrakis [3, (3, 5-di-tert-butyl-4-hydroxyphenyl)] pentaerythritol propionate;

[0033] Antioxidant B: tris(2,4-tert-butylphenyl) phosphite (ie);

[0034] Antioxidant C: dioctadecyl thiodipropionate.

[0035] The above-mentioned additives are respectively metered and added to the mixer for mixing and homogenization, and after two hours of homogenization, they are put into an extruder to be pressed into granular composite additives;

[0036] The above composite additives and polypropylene resin base material are measured separately, mixed uniformly, put into a twin-screw extruder for melt mixing and granulation. The residence time of the material in the screw is 2-4 minutes, the temperature of the screw is cont...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The melt flow rateaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method of producing high-gloss heat-resistance modification polypropylene resin, which comprises: polypropylene resin group material is mixed with additive uniformly before granulation is produced by melting and mixing. The polypropylene resin group material is isotactic and homopolymerized polypropylene with fused mass flowing speed of 3-26g / 10min and 98.5-99.5 percent of isotactic index. The additive comprises nucleating agent 2, 2-methylene-di (4, 6-di-tert-butylphenoxyl) sodium phosphate and 3MgO2.4SiO2.H2O; lubricant is monopalmitin; antioxidant is four (3, (3, 5-di-tert-buty-4-hydroxyphenyl)) propionate pentaerythritol ester, phosphorous acid three (2, 4-tert-butylphenyl) ester and thiodipropionate bisoctadecanol ester. The modified polypropylene resin produced by the invention not only has good heat resistance, but also has excellent luster of products, which can reach above 98 GU20 degrees.

Description

technical field [0001] The invention relates to a production method of modified polypropylene resin, in particular to a production method of polypropylene resin modified by heat resistance by adding additives such as nucleating agent, lubricant and antioxidant through melt mixing. Background technique [0002] Modified polypropylene has good physical properties and relatively low price. As a general-purpose plastic, its use has been continuously expanded. Among them, heat-resistant modified polypropylene has largely replaced ABS, PC and other materials in household appliances. manufacturing. The surface of household electrical appliances is usually required to have excellent gloss, otherwise it will not be possible to obtain a good appearance and touch. For the modification to improve heat resistance, in recent years, the method of adding nucleating agents is generally used. Nucleating agents can make polypropylene crystals finer and increase crystal density, thereby improv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08K5/524B29C47/92B29B9/06C08K5/521B29C48/92B29C48/95
CPCB29C48/92B29C2948/92704B29C48/04B29C2948/92561B29C2948/9259B29C2948/92885B29C2948/92895B29C48/95
Inventor 单国荣陈根荣高道春胡雄薛振忠刘林华
Owner SINOPEC SHANGHAI PETROCHEMICAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com