Reflection stacking acrylic paints for fine arts and method for manufacturing same

A technology of acrylic paint and manufacturing method, which is applied in the field of painting supplies, and can solve the problems of no accumulation effect and the like

Inactive Publication Date: 2011-02-09
宋健
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the prior art, the previous acrylic paint products for fine arts only present general visual effects under light in a dark environment, and there is no obvious three-dimensional accumulation effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of manufacturing method of reflective accumulation type acrylic paint for fine arts of the present invention adopts following process steps: its formula ratio is counted by mass parts:

[0033] Firstly, 1 part of hydroxyethyl cellulose and 2 parts of gum arabic were dispersed in 15 parts of distilled water of formula quantity, swelled for 6 hours, the temperature was heated to 85°C, and stirred until completely dissolved; 5 parts of glycerin, 0.3 parts of sodium benzoate and poly Combine 48 parts of acrylic emulsion (65 ± 2% solid content) and 8 parts of water-based polyurethane emulsion (30 ± 2% solid content) and mix to make an adhesive; add 16 parts of pigment powder titanium dioxide to the adhesive and stir evenly , then add 25 parts of calcium carbonate and stir evenly to form a color paste; add the color paste to the hopper of the three-roller grinder, and grind it 5 times through the three-roller grinder; the roll diameter of the three-roller grinder is 650...

Embodiment 2

[0035] A kind of manufacturing method of reflective accumulation type acrylic paint for fine arts of the present invention adopts following process steps: its formula ratio is counted by mass parts:

[0036] Firstly, 3.5 parts of hydroxyethyl cellulose and 2.5 parts of gum arabic were dispersed in 10 parts of distilled water of formula quantity, swelled for 8 hours, the temperature was heated to 88°C, and stirred until completely dissolved; 4 parts of glycerin, 0.2 parts of sodium benzoate and poly Combine 46 parts of acrylic emulsion and 10 parts of water-based polyurethane emulsion and stir evenly to make an adhesive; add 13 parts of pigment powder CI Pigment Blue and 3.0 parts of iron oxide to the adhesive and stir evenly, then add 26 parts of calcium carbonate and stir evenly Color paste: Add the color paste to the hopper of the three-roll mill, and grind it 5 times through the three-roll mill; the diameter of the three-roll mill roll is 650 mm, and the three-roll speed is ...

Embodiment 3

[0037] Embodiment three: a kind of manufacture method of reflective accumulation type acrylic paint for art of the present invention adopts the following process steps: its formula ratio is counted in parts by mass:

[0038] First, 4.0 parts of hydroxyethyl cellulose and 3.0 parts of gum arabic were dispersed in 12 parts of distilled water of the formula, swelled for 10 hours, heated to 90°C, and stirred until completely dissolved; 5.5 parts of glycerin, 0.25 parts of sodium benzoate and poly 42 parts of acrylic emulsion and 12 parts of water-based polyurethane emulsion were combined and stirred evenly to make an adhesive. Add 16 parts of pigment powder copper phthalocyanine blue B to the binder and stir evenly, then add 27 parts of calcium carbonate and stir evenly to form a color paste. Add the color paste material into the hopper of the three-roll mill, and grind it 5 times through the three-roll mill; the diameter of the three-roll mill roll is 650 mm, and the three-roll s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to art reflective accumulated acrylic paints with nano-pigment and the preparation method, belonging to technical field of painting things, which is characterized in that the hydroxyethylcellulose and the gum arabic are put into distilled water first and then dissolved by swelling, heating and blending. The glycerin and the sodium benzoate are mixed with the polyacrylic acidlatex and the aqueous polyurethane emulsion and the bond can be made by blending evenly. The powdered pigment is added into the bond and then blended evenly and the color sizing agent can be obtainedby blending after adding the calcium carbonate in. The color sizing agent is grinded in the hopper of a three-roller muller and then added in ethanol and glass microballoon. The product can be obtained after blending in a vacuum mixer. The preparation method can produce solid accumulation and splendent result by lighting in dark environment when painting by oil painting knife or paintbrush. The whole image can show splendent result, which can show the infectivity and the attraction of the artwork better.

Description

technical field [0001] The invention relates to a reflective stacking type acrylic paint for art and a manufacturing method thereof, specifically belonging to the technical field of painting supplies. Background technique [0002] In the prior art, the previous acrylic paint products for fine arts only present general visual effects under light in a dark environment, and there is no obvious three-dimensional accumulation effect. At present, in the production of art pigments, most of the high-shear mixers such as three-roll mills, high-speed dispersers, colloid mills, and homogenizers are used. The beads shatter and lose their spherical reflective properties. Contents of the invention [0003] The purpose of the present invention is to overcome the above disadvantages, thereby providing a reflective accumulation type acrylic paint for art and its manufacturing method, which uses high solid content polypropylene emulsion to cooperate with water-based polyurethane emulsion a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/06C09D133/02C09D7/12C09D175/04C09D101/26
Inventor 宋健
Owner 宋健
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com