Electrostatic resistance rubber material and preparation method thereof

A rubber material and antistatic technology, which is applied in the field of rubber materials and its preparation, can solve problems such as low heat resistance, poor antistatic effect, and unstable electrical performance, and achieve good antistatic performance, high antistatic efficiency, and good compatibility effect

Inactive Publication Date: 2008-09-10
SHANGHAI UNIV OF ENG SCI
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the antistatic agent commonly used in China is a quaternary ammonium salt surfactant with Cl- as an anionic group, but it has the disadvantages of poor antistatic effect, unstable electrical performance and low heat resistance, and it cannot be completely It meets the application requirements of the electronic and electrical industries with high antistatic requirements, and needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Disperse 10g of diethylamine and 10g of lead acetate in 30g of acetonitrile solvent and stir for 0.5 hours; then add 30g of sodium dodecylsulfonate and stir for 1 hour, the whole system becomes a viscous liquid, and the desired antibacterial Static agent.

[0037] Will 3 # Smoked sheet glue: 100 parts; sulfur: 2.0 parts; accelerator M: 0.5 parts; accelerator DM: 0.5 parts; accelerator CZ 0.5 parts, stearic acid: 0.6 parts; 0.8 part; Antistatic agent: 3 parts; Light calcium carbonate: 50 parts, place in the open mill, mix (mixing adopts traditional method) at the temperature of 30 ℃, obtain antistatic rubber of the present invention .

[0038] The surface resistivity test was carried out according to GB11210-89 standard, and the results are shown in Table 1.

Embodiment 2

[0040] Disperse 15g of isopropylamine and 15g of mercuric chloride in 30g of methanol solvent, and stir for 1 hour; then add 30g of alkylphenol polyoxyethylene ether and stir for 2 hours, and the whole system becomes viscous liquid, and the required antibacterial Static agent.

[0041] Will 3 # Smoked sheet rubber: 100 parts; sulfur: 3.0 parts; accelerator M: 1.0 parts; accelerator DM: 0.8 parts; accelerator CZ 1 part, stearic acid: 1.2 parts; 1.1 part; antistatic agent: 4 parts; light calcium carbonate: 35 parts, place in the open mill, mix (mixing adopts traditional method) at the temperature of 45 ℃, obtain antistatic rubber of the present invention .

[0042] The surface resistivity test was carried out according to GB11210-89 standard, and the results are shown in Table 1.

Embodiment 3

[0044] Disperse 20g of n-butylamine and 20g of silver nitrate in 30g of methanol solvent and stir for 1.5 hours; then add 30g of polyvinyl alcohol and stir for 3 hours to obtain the required antistatic agent.

[0045] Will 3 # Smoked sheet rubber: 100 parts; sulfur: 4.0 parts; accelerator M: 1.5 parts; accelerator DM: 1.0 parts; accelerator CZ 1.5 parts, stearic acid: 2.0 parts; 1.5 parts; antistatic agent: 5 parts; light calcium carbonate: 20 parts, place in the open mill, mix (mixing adopts traditional method) under the temperature of 55 ℃, obtain antistatic rubber of the present invention .

[0046] The surface resistivity test was carried out according to GB11210-89 standard, and the results are shown in Table 1.

[0047] Table 1

[0048] Comparative example 1

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides antistatic rubber material and a preparation method thereof, wherein the antistatic rubber material contains antistatic agent of 3 to 5 weight percent with reference to rubber matrix of 100 weight percent; the antistatic agent is a mixture and comprises compositions according to the following weight ratio: emulsifying agent: polar solvent: organic amine: metal salt is equal to 3:3:1-2:1-2; and the metal salt is selected from lead acetate, mercury bichloride, copper sulphate, iron chloride, antimonic chloride, stannic chloride or silver nitrate. The rubber material prepared by the antistatic agent has excellent antistatic performance, surface resistivity reaching 10<6> ohm to 10<8> ohm as well as high-efficient and persistent static resistance; moreover, the rubber material has ideal compatibility with other additives of rubber products, thereby meeting the requirements of high temperature during manufacturing the rubber products without influencing the physical property and the chemical property of one another.

Description

technical field [0001] The invention relates to a rubber material containing an antistatic agent and a preparation method thereof. Background technique [0002] Rubber is the basic raw material of the rubber industry and is widely used in the manufacture of tires, hoses, tapes, cables and other rubber products. Rubber has excellent insulating properties, which will cause a large amount of static electricity to accumulate, which is a serious defect in the application of its products in the electronics industry. For example: These static electricity will generate gravitational force and absorb dust, pollute integrated circuits and semiconductor components, and greatly reduce the yield of electronic products; electrostatic discharge will cause failure or malfunction of electronic equipment, causing electromagnetic interference; high-voltage electrostatic discharge will cause Electric shock, causing explosion and fire, endangering personal safety. Therefore, how to reduce and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/06C08L9/02C08K13/02C09K3/16
Inventor 王锦成高芝君周一鸣
Owner SHANGHAI UNIV OF ENG SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap