Water resistance tree medium voltage insulated cable material and cable
A technology for insulating cables and water tree resistance, which is used in plastic/resin/wax insulators, organic insulators, etc. to achieve good water solubility, good compatibility, and perfect crystal structure.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0040] Example 1: Preparation of Organized Montmorillonite by Microwave
[0041] Add 25g of montmorillonite and 750g of deionized water, heat up to 75 degrees, add dropwise a 20% aqueous solution containing 12g of dinonyldimethylammonium bromide. After the addition is complete, treat with microwave for 7 minutes every 45 minutes , Stir for 5 hours, filter with suction, wash the precipitate with deionized water, silver nitrate (0.1mol / L) can not detect bromide ions, vacuum dry to constant weight, grind and sieving through 200 meshes to obtain organically modified montmorillonite earth.
Example Embodiment
[0042] Example 2: Preparation of medium voltage cross-linked polyethylene insulated cable material
[0043] The formula composition of the weight parts of the medium voltage cross-linked polyethylene insulated cable material:
[0044] Low density polyethylene 100 parts
[0045] Dicumyl peroxide 1.8 parts
[0046] 0.6 parts of di-tert-butylperoxycumene
[0047] 0.1 part of tris(2,4-di-tert-butylphenyl) phosphite
[0048] 4,4'-thiobis(3-methyl-6-tert-butylphenol) 0.3 parts
Example Embodiment
[0049] Example 3-9: According to Example 2, the formula of the compound water tree growth agent was changed to prepare the water tree resistant medium pressure cross-linked polyethylene insulated cable material, as shown in Table 1:
[0050] Table 1. Medium voltage insulated cable materials prepared by adding different water tree growth agents with reference to the basic formula of Example 2
[0051] Example
[0052] Weight unit in the table: parts
[0053] It can be seen from Table 1 that the addition of the compound type water tree resistance agent has significantly better water tree resistance performance than a single water tree resistance agent.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap