Styling compositions and their uses

A composition and application technology, applied in the field of furnace-hardenable modeling compositions, can solve problems such as damage to hormones or reproduction, slow hardening process, insufficient breaking strength, etc., and achieve the effect of being easy to operate with bare hands

Inactive Publication Date: 2011-12-28
STAEDTLER MARS GMBH & CO KG
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of such compositions is that they harden only at very high temperatures, wherein the hardening process takes place slowly
For this reason, the fracture strength of such hardened compositions is insufficient
Furthermore, disadvantageously, such compositions have a content of up to 30% by weight of phthalate-containing plasticizers, which are suspected of having hormonal or reproductively damaging effects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Formulation Example 1: Unpigmented Composition

[0042] 65% by weight PVC or PVC copolymer

[0043] 19% by weight of adipic acid-based plasticizer

[0044] 7% by weight stabilizer

[0045] 19% by weight talc

Embodiment 2

[0046] Formulation Example 2: Red Composition

[0047] 63% PVC by weight

[0048] 24% by weight of citric acid-based plasticizer

[0049] 1% by weight stabilizer

[0050] 7% by weight costabilizer

[0051] 4% filler by weight

[0052] 1% by weight Pigment Red 254

Embodiment 3

[0053]Formulation Example 3: Yellow Composition

[0054] 65% PVC by weight

[0055] 21.5% by weight of citric acid-based plasticizer

[0056] 1.5% by weight costabilizer

[0057] 5.5% by weight stabilizer

[0058] 6.0% by weight of fillers (chalk, silica)

[0059] 0.5% by weight of Pigment Yellow 83

[0060] Prior Art: Ocher Color Contrast Formula

[0061] 15kg emulsion PVC

[0062] 17kg suspension PVC

[0063] 2.5kg calcium stearate

[0064] 13.5kg di-n-octyl phthalate (plasticizer)

[0065] 1kg fatty acid octyl ester

[0066] 14kg aluminum silicate

[0067] 0.5kg of pigment (ocher mixture)

[0068] In a preferred embodiment, the content of plasticizer is between 10 and 28% by weight, in a particularly preferred embodiment between 15 and 24% by weight.

[0069] Phthalate-free plasticizers used with preference are based on citric acid and / or adipic acid.

[0070] The desired consistency of the composition can be adjusted without problems by varying the content of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A modelling material contains a binder in the form of a plastisol, wherein the plastisol contains essentially PVC (polyvinyl chloride) and at least one phthalate-free plasticizer. The phthalate-free plasticizer is citric acid-based, adipic acid-based, or benzoate ester-based. The material contains 5% by weight to 95% by weight PVC; 5% by weight to 30% by weight phthalate-free plasticizer; 0% by weight to 10% by weight stabilizer; 0% by weight to 10% by weight co-stabilizer; 0% by weight to 75% by weight fillers; 0% by weight to 5% by weight coloring agent; and 0% by weight to 5% by weight other additives.

Description

technical field [0001] The invention relates to oven-hardenable styling compositions and their use. Background technique [0002] Plastic, oven-hardenable compositions for shaping and molding objects are known in principle. [0003] Styling compositions are also to be understood as so-called clays or, in the case of polymer-containing compositions, polymer clays. [0004] Thus, plastic, hand-mouldable and heat-hardenable compositions are known from DE 25 15 757 C3. Such compositions mainly consist of polyvinyl chloride, fillers and plasticizers. The disadvantage of such compositions is that they harden only at very high temperatures, wherein the hardening process takes place slowly. For this reason, the fracture strength of such hardened compositions is insufficient. Furthermore, it is disadvantageous that such compositions contain up to 30% by weight of phthalate-containing plasticizers, which are suspected of having hormonal or reproductively damaging effects. [0005...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K5/00
CPCC08J3/18C08K5/0016C08K5/11C08J2327/06C08L27/06C08K5/00C08K5/10C08K5/09
Inventor Y·弗雷泽I·罗伊特H·施诺雷尔
Owner STAEDTLER MARS GMBH & CO KG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com