Method for producing stainless steel composite steel plate

A technology of clad steel plate and manufacturing method, which is applied in the direction of manufacturing tools, metal rolling, non-electric welding equipment, etc., can solve the problems such as limiting the application range of stainless steel clad steel plate, and achieve high bonding rate, high thermal conductivity, and uniform cladding thickness. Effect

Active Publication Date: 2009-01-28
TAIYUAN IRON & STEEL GROUP
View PDF0 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The stainless steel clad steel plate produced by the method of producing stainless steel medium and thick steel plate by the existing explosion method cannot meet the needs of these fields, which limits the application range of the stainless steel clad steel plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing stainless steel composite steel plate
  • Method for producing stainless steel composite steel plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The materials of the base plate and double board are shown in Table 1.

[0043] Table 1

[0044] Numbering

material

Thickness mm

Length mm

Width mm

A side double board

0Cr18Ni9

14

4430

1270

Substrate

10Al

90

4430

1270

Side B double board

0Cr18Ni9

14

4470

1270

[0045] The manufacturing method embodiment of this stainless steel cold-rolled clad steel plate is the following steps in sequence:

[0046] 1. Match

[0047] The stainless steel 0Cr18Ni9 and ordinary carbon steel plate 10Al that meet national standards and technical requirements will be inspected, and the stainless steel plate and steel plate will be combined according to the final product and rolling requirements. Two 0Cr18Ni9 stainless steel cladding plates and one 10Al ordinary carbon steel plate form a group .

[0048] 2. Carbon steel strips are welded around the cladding plate

[0049] Weld car...

Embodiment 2

[0070] The materials of the substrate and doubler board are shown in Table 2.

[0071] Table 2

[0072] Numbering

material

Thickness mm

Length mm

Width mm

A side double board

304

14

4430

1270

Substrate

08Al

90

4430

1270

Side B double board

304

14

4470

1270

[0073] The manufacturing method of this stainless steel cold-rolled clad steel plate differs from Example 1 in two points. The first is that the materials of the base plate and the A-side doubler plate and the B-side doubler plate are different, and the second is that the hot-rolled steel plate is solution pickled in step eight. Finally, there are cold rolling and cold rolling solution pickling, and then inspection and finishing. The first eight steps of this embodiment are the same as those of the embodiment, that is, 1. Matching; 2. Welding carbon steel strips around the doubler plate; 3. Grinding; 4. Explosive...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

A method for manufacturing a compound steel plate of stainless steel includes the following steps in turn: I, matching two stainless steel plates with a common carbon steel plate and carrying out fitting up according to the demands of a final finished product and rolling; II, welding carbon steel strips on the surrounding of the compound plate: welding the common carbon steel strips with a thickness of 6-8mm and a width of 60mm on the surrounding of the non-junction surface of the compound plate; III, polishing: using a sander to remove the impurities like oxide on the junction surface; IV, explosion welding: welding the compound plate of A surface on a basic plate firstly, and then welding the compound plate of B surface in an explosion way; V, fault detection: using an ultrasonic defectoscope to carry out fault detection; the area junction rate between the compound plate and the basic plate is not less than 99 percent; VI, carrying out defected weldseams on the surrounding fault; VII, carrying out hot rolling on the compound steel plate; feeding the compound steel plate into a hot milling roll to be rolled into a hot rolling compound steel bend with a thickness not more than 3mm; VIII, carrying out hot rolling, solid solution and acid cleaning on the steel plate and finally finishing the steel plate. The manufacture method of the invention can be used for manufacturing the compound steel plate of stainless steel with a total thickness of 0.8mm to 2mm.

Description

technical field [0001] The invention relates to a method for manufacturing a stainless steel clad steel plate. Background technique [0002] Stainless steel clad plate is a new type of material that is energy-saving and environmentally friendly. At present, the direct explosion method is mainly used to produce stainless steel medium-thick steel plates in China. It is mainly used in petrochemical, water conservancy, and salt production. The characteristics of this production method require that the clad layer is thicker (≥ 2mm), which limits the application range of the stainless steel clad steel plate. In light industrial machinery, food, cooking utensils, construction, decoration, welded pipes, railway passenger cars, medical and health, environmental protection and other industries, what is more needed is a stainless composite steel cold steel with a total thickness of less than 2mm, especially less than 1.2mm. Rolling of thin steel sheets and strips. The stainless steel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23P17/00B23K20/08B21B1/38C21D8/02C23G1/08
Inventor 赵阳囤王立新范述宁
Owner TAIYUAN IRON & STEEL GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com