Anti-yellowing polychloroethylene

A polyvinyl chloride, anti-yellowing technology, applied in the field of polyvinyl chloride, can solve problems such as non-conformity, abrupt appearance, yellowing, etc., and achieve good anti-yellowing characteristics, good implementation effect, and good weather resistance

Inactive Publication Date: 2011-06-08
TAIZHOU FENGYUAN SANITARY CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, most of the anti-yellowing PVC wire and cable materials are mostly dark-colored, and it is easy to appear abrupt for some installation locations that require a latent color appearance.
And after a long time of use, even the darkest color will inevitably appear a lot of yellowing, lacking a long-lasting anti-yellowing
At the same time, the anti-yellowing polyvinyl chloride products on the market are relatively deficient in weather resistance and migration resistance, and cannot be applied to the manufacturing and application fields of wires and cables, nor do they meet the requirements of UL62, UL83, UL758 and UL1581 standards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The processing steps are as follows: First, add polyvinyl chloride resin, plasticizer, stabilizer, antioxidant, ultraviolet absorber, lubricant, pigment, calcium carbonate filler and other additives into the high-mixer according to the ratio in the table mix.

[0032] components

[0033] plasticizer

[0034] After that, after the temperature of the material in the high mixer rises to 100°C, put the material in the high mixer into the cooling mixer. Next, after the material is cooled and mixed to about 45°C, the material in the cooling mixer is discharged. Subsequently, the mixed materials are fed into an extrusion granulator, and the temperature of the extruder barrel and head is controlled within the range of 135-150°C. Finally, the prepared pellets are cooled and dried, and the dried pellets are the anti-yellowing polyvinyl chloride involved in the present invention.

Embodiment 2

[0036] The processing steps are as follows: First, add polyvinyl chloride resin, plasticizer, stabilizer, antioxidant, ultraviolet absorber, lubricant, pigment, calcium carbonate filler and other additives into the high-mixer according to the ratio in the table mix.

[0037] components

[0038] components

[0039] other

[0040] The remaining steps are the same as those in Embodiment 1 and will not be repeated here.

Embodiment 3

[0042] The processing steps are as follows: First, add polyvinyl chloride resin, plasticizer, stabilizer, antioxidant, ultraviolet absorber, lubricant, pigment, calcium carbonate filler and other additives into the high-mixer according to the ratio in the table mix.

[0043] components

Weight(KG)

percentage(%)

PVC

100

45

plasticizer

60

27

stabilizer

3

1.4

antioxidant

0.3

0.14

UV absorber

4

1.8

lubricant

0.5

0.23

pigment

0.2

0.09

calcium carbonate

44

19.8

other

10

margin

[0044] The remaining steps are the same as those in Embodiment 1 and will not be repeated here.

[0045] To sum up, the present invention adopts a scientific formula, which can make polyvinyl chloride achieve better anti-yellowing characteristics, and more importantly, the finished product of polyvinyl ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention relates to anti-yellowing PVC which belongs to the technical field of organic polymer compounds. The invention comprises the following components (weight percent): 41 to 50 percent of PVC, 24 to 30 percent of plasticizer, 1 to 3 percent of stabilizer, 0.1 to 0.2 percent of antioxidant, 1 to 4 percent of UV absorbent, 0.1 to 1 percent of lubricant, 0.03 to 0.1 percent of pigment, and15 to 20 percent of filler. The invention can cause the PVC to achieve better anti-yellowing property, and the finished goods are white and have good weather and transfer resistance effects.

Description

technical field [0001] The invention relates to a polyvinyl chloride, in particular to an anti-yellowing, weather-resistant and migration-resistant polyvinyl chloride, which belongs to the technical field of organic polymer compounds. Background technique [0002] At present, most anti-yellowing polyvinyl chloride wire and cable materials are mostly dark-colored, which is easy to appear abrupt for some installation locations that require a latent color appearance. And after a long time of use, even the darkest color will inevitably show a lot of yellowing, lacking a long-lasting anti-yellowing. At the same time, the existing anti-yellowing PVC products on the market lack weather resistance and migration resistance, which cannot be applied to the manufacturing and application of wire and cable, and do not meet the requirements of UL62, UL83, UL758 and UL1581 standards. Contents of the invention [0003] The object of the present invention is to provide a kind of polyvinyl ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K5/524C08K3/26C08K3/22C08K5/20C08K5/09C08L67/02C08L27/06
Inventor 侯永刚
Owner TAIZHOU FENGYUAN SANITARY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com