Annealing method of cast-rolling aluminum foil used for air conditioner radiation fin

A heat sink and air conditioner technology, which is applied in the field of annealing, can solve problems such as uneven mechanical properties of aluminum foil, oil spots on the surface of aluminum foil, and low production efficiency, and achieve significant production benefits, prevent oil spots, and improve utilization.

Active Publication Date: 2010-06-02
包头常铝北方铝业有限责任公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the annealing of aluminum foil for air conditioner heat sinks mainly adopts the method of low-temperature and long-term heat preservation annealing. This method has the following disadvantages: abnormally coarse grains and low elongation are prone to occur during the annealing process ; The mechanical properties of the aluminum foil in the same furnace are not uniform; there are oil spots on the surface of the aluminum foil; at the same time, the annealing cycle is long and the production efficiency is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Finished annealing method for producing 3102H26 aluminum foil for air conditioner radiator using cast-rolled blanks: quickly heat up to 200°C, keep it warm for 1 hour; continue to heat up to 318°C, then keep it warm for 100 minutes; cool down to 268°C, keep it warm for 5 hours and then air-cooled . The mechanical properties of the annealed aluminum foil are: tensile strength 135-145MPa, elongation ≥15%, cupping value ≥6.0mm.

Embodiment 2

[0014] Finished annealing method for producing 3102H26 aluminum foil for air conditioner radiator using cast-rolled blanks: Rapidly heat up to 210°C and keep it warm for 2 hours; continue to heat up to 335°C and then keep it for 100 minutes; cool down to 275°C and keep it warm for 5 hours before air cooling . The mechanical properties of the annealed aluminum foil are: tensile strength 130-140MPa, elongation ≥17%, cupping value ≥6.5mm.

Embodiment 3

[0016] Finished annealing method for producing 8011H22 aluminum foil for air conditioner radiator using cast-rolled billet: quickly heat up to 230°C, keep it warm for 1 hour; continue to heat up to 355°C, then keep it for 120 minutes; cool down to 280°C, keep it warm for 3 hours and then air-cooled . The mechanical properties of the annealed aluminum foil are: tensile strength 118-128MPa, elongation ≥20%, cupping value ≥7.4mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for annealing a rolling-casting aluminum foil used for an air conditioner radiating plate, which is characterized by comprising the following steps: 1) raising the furnace gas temperature of an annealing furnace to between 200 and 230 DEG C and keeping the temperature for 1 to 3 hours; 2) raising the furnace gas temperature of the annealing furnace to between 316 and 375 DEG C and keeping the temperature for 80 to 200 minutes; and 3) reducing the furnace gas temperature of the annealing furnace to between 266 and 300 DEG C and keeping the temperature for 3 to 5hours. The method adopts a differential temperature annealing process to raise the furnace gas temperature of the annealing furnace so that the speed of temperature rise is increased, the nucleating rate of the internal grain structure of the aluminum foil is larger than the growth rate to achieve recrystallization, and the crystallizing structure is tiny and uniform to achieve the optimal mechanical property; besides, belt oil on the material surface is volatilized to effectively prevent the defects of oil spot and the like on the surface of the aluminum foil, ensure that the quality of the surface of the aluminum foil is good, shorten the total time for annealing the aluminum foil, and improve the production efficiency.

Description

Technical field [0001] The invention relates to an annealing method, in particular to an annealing method of cast-rolled aluminum foil for heat sinks of air conditioners. Background technique [0002] After more than ten years of development, China has become a major manufacturer of air conditioner heat exchangers, accounting for about 67% of the world's total output. In 2007, it is estimated that 60 million air conditioners will be produced in China, which is truly the world's largest in terms of output. 1. But like all home appliance industries, China is definitely a big air-conditioning country, but not a strong air-conditioning country. The most important thing is that the technology level of the material industry is very different from that of developed countries. Air conditioners are already indispensable electrical appliances in people’s lives. Air conditioner radiators are one of the main parts of air conditioners. Therefore, the amount of aluminum foil used for air condi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22F1/04
Inventor 章建华何献忠彭晓彤
Owner 包头常铝北方铝业有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com