Non-floating bead low-density cement mortar

A non-floating bead low, cement slurry technology, applied in the field of cement, can solve the problem of not being able to maintain the design density

Inactive Publication Date: 2009-07-08
DAQING OILFIELD CO LTD +1
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to overcome the problem that the cement slurry in the background technology cannot maintain its design density under high pressure conditions, and provides a non-bleaching low-density cement slurry, the density of which is 1.40-1.55g / cm 3 It is incompressible within the range, and the price is low, and the cementing cost is low, so as to meet the technical needs of oilfield exploration and development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-floating bead low-density cement mortar
  • Non-floating bead low-density cement mortar
  • Non-floating bead low-density cement mortar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: The components and proportioning of the non-bleaching low-density cement slurry are as follows in parts by weight: 100 parts of cement, 321 parts of water, 121 parts of fly ash, 36 parts of silica fume, 36 parts of superfine cement, early strength agent 10 parts, according to the above ratio, mix the external admixture fly ash, silica fume, ultra-fine cement, early strength agent and cement according to the required ratio, and mix it with an appropriate amount of water evenly. The strength of the prepared cement slurry measured at 80°C is 15.4MPa.

Embodiment 2

[0013] Embodiment 2: The non-floating pearl low-density cement slurry components and proportioning are as follows by weight: 100 parts of cement, 321 parts of water, 136 parts of fly ash, 36 parts of silica fume, 36 parts of superfine cement, early strength agent 10 parts were uniformly mixed as in Example 1, and the strength of the prepared cement slurry measured at 80°C was 15.8 MPa.

Embodiment 3

[0014] Embodiment 3: The non-floating pearl low-density cement slurry components and proportioning are as follows by weight: 100 parts of cement, 321 parts of water, 129 parts of fly ash, 33 parts of silica fume, 36 parts of superfine cement, early strength agent 10 parts were uniformly mixed as in Example 1, and the strength of the prepared cement slurry measured at 80° C. was 15.2 MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Strengthaaaaaaaaaa
Strengthaaaaaaaaaa
Strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a non-cenosphere light weight cement slurry, which mainly solves the problem that the cement slurry cannot keep the density thereof under a high pressure condition. The non-cenosphere light weight cement slurry is characterized by comprising the following components in portion by weight: 100 portions of cement, 116 to 321 portions of water, 52 to 136 portions of fly ash, 14 to 38 portions of silica fume, 14 to 38 portions of superfine cement, and 6 to 11 portions of early strength agent, wherein the particle diameter of the silica fume (of which the SiO2 content is more than 90 percent) is more than 0 and less than 0.5 mu m, the particle density of the silica fume and the fly ash is 2.0 grams per cubic meter, and the particle diameter of the superfine cement is more than 0 and less than 2 mu m. The light weight cement slurry forms a set of incompressible light weight cement slurry system of which the density is between 1.40 and 1.55 grams per cubic meter through preferentially selecting external additives and applying a grain composition principle, wherein the flowability and the sedimentation stability of the cement slurry are good, the set cement strength is more than 15 MPa and cannot decline at a temperature of 150 DEG C so as to satisfy the technical requirements on oil field exploration and development.

Description

Technical field: [0001] The invention relates to a cement used in the field of oil field drilling and cementing, in particular to a non-floating bead low-density cement slurry. Background technique: [0002] In the field of oilfield drilling and cementing, the oil and gas layers are widely distributed, and there are more and more long-sealed wells. One of the main methods used in long-sealing well cementing is to use low-density cement slurry for well cementing. At present, low-density cement slurry with floating beads is widely used in oil fields, but due to the existence of floating beads, the cement slurry cannot maintain its properties under high pressure conditions. Design density, as the pressure rises, the density of cement slurry increases, and the fluidity of cement slurry also deteriorates greatly, which brings unsafe factors to the cementing construction of deep wells in oil fields; and because floating beads are industrial by-products of power plants, With the i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00C04B18/08C04B14/04
CPCC04B2201/50C04B2201/20C04B28/02Y02W30/91C04B7/527C04B18/08C04B18/146C04B2103/12
Inventor 贾维君杨智光吴广兴李晓琦段治华金永男耿建卫姜增东
Owner DAQING OILFIELD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com