A liquid colloid filling low-temperature well-cementing cement mortar system

A technology for cementing cement slurry and colloid, which is applied in the field of oil and gas well cementing, can solve the problems of difficulty in obtaining anti-channeling ability and early strength, high cost of fast-hardening cement, and difficulty in adjustment, and achieves good settlement stability and increased gas resistance. The effect of channeling performance and convenient on-site construction

Inactive Publication Date: 2017-05-10
CHINA UNIV OF PETROLEUM (EAST CHINA)
View PDF11 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the early strength of the rapid-hardening cement system develops rapidly, but there are problems of short thickening time and difficult adjustment, and the cost of rapid-hardening cement is high; the existence of foam in the foam cement slurry system makes the stability of the cement slurry worse. , the early strength and final strength of cement stone are low, and the foam cement slurry system requires additional equipment and technical personnel, and the construction cost is high; the particle size optimized cement system with ultrafine cement or ultrafine particles can be used at low temperature and low density. It is difficult to obtain better anti-channeling ability and early strength; the ultrafine slag cement system has poor rheological properties and cannot guarantee the later strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A liquid colloid filling low-temperature well-cementing cement mortar system
  • A liquid colloid filling low-temperature well-cementing cement mortar system
  • A liquid colloid filling low-temperature well-cementing cement mortar system

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Cement slurry formula: 100 parts of Portland cement (label: P.O 52.5R) produced by Henan Mengdian Cement Factory, 80 parts of lynx brand superfine Portland cement (model: 1250) produced by Shandong Yingan Environmental Protection Material Technology Co., Ltd. 10 copies of hollow glass microspheres (model: Y8000) produced by Sinosteel Maanshan Mining Institute New Material Technology Co., Ltd., 10 copies of Sepsen brand micro-silicon provided by Shandong Boken International Trade Co., Ltd., Zhejiang Yuda Chemical Co., Ltd. 10 parts of silica sol (model: GS-35) produced by the company, 4 parts of early strength agent sodium sulfate, 1 part of polycarboxylate water reducer, 2 parts of water loss reducer, 1 part of tributyl phosphate defoamer , 120 parts of water.

[0042] Preparation method: dissolve early strength agent, water reducer, water reducing agent, defoamer and silica sol in water, and then prepare cement slurry with the obtained aqueous solution and cement accor...

Embodiment 2

[0047] Cement slurry formula: 100 parts of Shengwei G-grade cement produced by Shandong Shengwei Cement Factory, 80 parts of Lynx brand superfine Portland cement (model: 1250) produced by Shandong Yingan Environmental Protection Material Technology Co., Ltd., Ma'anshan, China Steel Group 10 parts of hollow glass microspheres (model: Y8000) produced by Mining Institute New Material Technology Co., Ltd., 10 parts of Sepsen brand micro-silicon provided by Shandong Boken International Trade Co., Ltd., silica sol produced by Zhejiang Yuda Chemical Co., Ltd. ( Model: GS-35) 10 parts, early strength agent sodium sulfate 4 parts, polycarboxylate water reducer 1 part, fluid loss reducer 2 parts, tributyl phosphate defoamer 1 part, water 120 parts.

[0048] Preparation method: dissolve early strength agent, water reducer, water reducing agent, defoamer and silica sol in water, and then prepare cement slurry with the obtained aqueous solution and cement according to API 10B-3-2004 oil wel...

Embodiment 3

[0051] Cement slurry formula: 180 parts of Portland cement (label: P.O 52.5R) produced by Henan Mengdian Cement Factory, 10 parts of hollow glass microspheres (model: Y8000) produced by Sinosteel Maanshan Mining Institute New Material Technology Co., Ltd. , 10 parts of Sepsen brand micro-silicon provided by Shandong Boken International Trade Co., Ltd., 10 parts of silica sol (model: GS-35) produced by Zhejiang Yuda Chemical Co., Ltd., 4 parts of early strength agent sodium sulfate, polycarboxylic acid 1 part of salt water reducer, 2 parts of fluid loss reducer, 1 part of tributyl phosphate defoamer, 120 parts of water.

[0052] Preparation method: dissolve early strength agent, water reducer, water reducing agent, defoamer and silica sol in water, and then prepare cement slurry with the obtained aqueous solution and cement according to API 10B-3-2004 oil well cement test method.

[0053] Refer to the standard SY / T 6544-2003 oil well cement slurry performance requirements to me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

A liquid colloid filling low-temperature well-cementing cement mortar system is provided. The system is characterized in that the system includes 100 parts by mass of Portland cement, 80-120 parts by mass of ultrafine Portland cement, 10-30 parts by mass of hollow glass microbeads, 10-20 parts by mass of micro-silicon, 8-12 parts by mass of liquid colloid, 2-6 parts of an early strength agent, 1-2 parts by mass of drag reducer, 4-8 parts by mass of a water loss reducing agent, 1-2 parts by mass of a defoamer and 120-150 parts of water. According to the system, the density of the system is adjustable in a range of 1.35-1.65 g/cm<3>, the low-temperature early strength is high, thickening performance and fluidity are good, the water loss amount is low, and the system has excellent anti-fluid-channeling performance, can be used for well cementing for deepwater surface layer sections, can save working time and costs and can provide safe and efficient technical supports for deepwater oil and gas exploitation.

Description

technical field [0001] The invention relates to a low-temperature cementing slurry system filled with liquid colloid, and belongs to the technical field of oil and gas well cementing. It is especially suitable for deep water shallow layer cementing operations with low temperature, low fracture pressure, and prone to water-gas channeling, and it can also be used for surface layer cementing in cold areas of onshore oilfields. Background technique [0002] With the development of global onshore oil and gas resources becoming more and more mature, oil and gas production continues to decline, and the direction of exploration and development of oil and gas resources is constantly shifting to offshore oil and gas. The global marine oil and gas reserves are about 100 billion tons, and the proven reserves are more than 38 billion tons. The natural gas reserves are about 140 trillion cubic meters, and the proven reserves are about 40 trillion cubic meters. At present, 80% of the prov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K8/467C09K8/473C09K8/48C09K8/487C09K8/493C04B28/04
CPCC09K8/467C09K8/473C09K8/48C09K8/487C09K8/493C04B28/04C04B2201/50C04B2201/20C04B2111/00724C04B14/24C04B18/146C04B22/06C04B22/147C04B2103/302C04B24/003C04B2103/46
Inventor 步玉环侯献海孙健翔赵乐天邵子璇
Owner CHINA UNIV OF PETROLEUM (EAST CHINA)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products