Polypropylene resin blend and preparing method thereof

A polypropylene resin and blend technology, applied in the field of polypropylene resin, can solve the problems of material thermal deformation temperature, rigidity reduction, appearance defects of striped lines, failure to meet appearance requirements, etc., and achieve excellent rigidity-toughness balance and appearance. Excellent effect with a wide range of process adjustment

Inactive Publication Date: 2009-10-07
贵州凯科特材料有限公司 +1
View PDF4 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] From the above analysis, it can be seen that conventional modified polypropylene materials have the defect of insufficient low-temperature toughness, and in order to achieve a certain low-temperature toughness, a large amount of rubber can be added,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene resin blend and preparing method thereof
  • Polypropylene resin blend and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 6

[0043] Embodiment 6: Raw materials: 65 kg of polypropylene, 10 kg of polyethylene, 10 kg of vinyl copolymer rubber (CA7320A), 15 kg of talcum powder (5 μm in particle size), 0.5 kg of polypropylene nucleating agent, and 0.5 kg of antioxidant. The preparation method is the same as above.

Embodiment 7

[0044] Example 7: Raw materials: 50 kg of polypropylene, 1 kg of polyethylene, 15 kg of vinyl copolymer rubber (8200), 30 kg of talcum powder (0.05 μm in particle size), 0.01 kg of polypropylene nucleating agent, and 0.1 kg of antioxidant. The preparation method is the same as above.

Embodiment 8

[0045] Embodiment 8: Raw materials: 80 kg of polypropylene, 15 kg of polyethylene, 25 kg of vinyl copolymer rubber (8200), 10 kg of talcum powder (particle size 0.1 μm), 1 kg of polypropylene nucleating agent, and 1 kg of antioxidant. The preparation method is the same as above.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polypropylene resin blend, which is prepared with polypropylene, polyethylene, vinyl co-polymer rubber, talcum powder, polypropylene and anti-oxidant. Compared to the existing technology, the polypropylene resin blend has excellent balance of rigidity and toughness, the low temperature notch impact strength is greatly higher than the general polypropylene composite materials, the crystallization rate is fast and crystal form is controllable, the period of injection molding is short, and there is no tiger skin veins on the surface of the injection molding articles, the heat resisting and oxidation susceptibility is excellent, can be processed in the higher molding temperature (higher than 240 Celsius system), therefore the adjusting range of this technology is large, and can be recovered many times. The blend is especially suitable for preparing instrument board of ensconcing safety airbag, the tensile strength of the blend is more than 20MPa, bend strength is more than 30MPa, the IZOD notch impact strength is more than 15KJ/m2 at the temperature of subzero 30 Celsius system.

Description

technical field [0001] The invention relates to the technical field of polypropylene resin, in particular to a polypropylene resin blend and a preparation method thereof. Background technique [0002] The passenger side of the car dashboard is usually equipped with an airbag. In order not to affect the integrity of the appearance of the dashboard, more and more models are equipped with hidden airbags. Generally, the airbag cover is integrated with the dashboard. A specific area of ​​the instrument panel skin is pre-weakened to form easy-to-tear nicks. When the airbag bursts, the pressure of the airbag deployment causes the pre-weakened nicks on the instrument panel to tear, and the airbag pops up and deploys to protect passengers. When the airbag explodes, if the toughness of the material is insufficient, the weakened area will often produce sharp fractures and even flying debris or broken particles, which may cause the airbag to be scratched and cause injury to the occupant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/06C08L23/08C08L23/16C08K3/34B29B9/06B29C47/92B29C48/40B29C48/92
CPCB29C48/92B29C48/04B29C48/40B29C48/625B29C2948/92514B29C2948/92914
Inventor 秦舒浩于杰陈兴江何敏姜岩世张敏敏
Owner 贵州凯科特材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap