Method for producing photocatalysis ceramics with adjustable surface gloss

A technology of photocatalytic ceramics and production methods, applied in chemical instruments and methods, physical/chemical process catalysts, titanium dioxide, etc., can solve problems such as gloss changes, achieve consistency, ensure decorative effects, and simple processes

Active Publication Date: 2009-10-28
FUZHOU UNIVERSITY +1
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

We have used the sol-gel method to develop a titanium dioxide sol-type photocatalyst. Although this photocatalyst can form a transparent and colorless film on the surface of ceramic tiles, it brings changes in the glossiness of the surface.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing photocatalysis ceramics with adjustable surface gloss
  • Method for producing photocatalysis ceramics with adjustable surface gloss

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The preparation method of the present invention is carried out according to the following steps:

[0012] (1) Carry out the preparation of catalyst first, prepare pure titanium dioxide sol, adjust the pH value of sol, make the sol-type titanium dioxide photocatalyst of corresponding pH value,

[0013] (2) Carry out the coating of catalyst, make the sol-type titanium dioxide photocatalyst by 5~50mL / m 2 The amount of the photocatalytic ceramics with adjustable surface gloss is obtained by spraying, pulling, brushing or dipping on the surface of the ceramics, and then heat-treated or directly dried. The heat treatment conditions are: 100-600 ° C, time 10 to 120 minutes.

[0014] The preparation of the above catalyst is to hydrolyze titanium alkoxide (such as tetraisopropyl titanate, tetrabutyl titanate) under the condition of acidic pH<5 to obtain a uniform and transparent sol, and adjust the sol by dialysis according to the glossiness. The pH value is a certain value in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for producing photocatalysis ceramics with adjustable surface gloss, which is characterized in that: the production method includes the following steps: (1) preparing catalyst at first, preparing pure titanic oxide sol, adjusting pH of sol, and producing sol type titanic oxide photocatalyst with corresponding pH value,(2) coating with sol type titanic oxide photocatalyst with dosage of 5-50 mL / m in spray finishing, lifting, brushing or dipping type on the surface of ceramics, for producing photocatalysis ceramic with adjustable surface gloss by heat-treatment or direct cooling and drying, wherein, the heat treat condition is: at 100-600 DEG C for 10-120 minutes. The method not only has simple steps, but also can be used for producing ceramics with required glossiness according to the design requirement.

Description

technical field [0001] The invention relates to a method for making photocatalytic ceramics with adjustable surface gloss Background technique [0002] Ceramic products are widely used in construction, decoration and daily life. Different use environments will bring dirt, germs and odors to the ceramic surface. It is of great significance to develop ceramic products with self-cleaning and antibacterial functions. In recent years, people have used the photocatalytic oxidation and photohydrophilic properties of titanium dioxide to coat it on the surface of materials to develop many functional materials, such as self-cleaning exterior wall tiles, self-cleaning glass curtain walls, antibacterial sanitary ware, etc. These materials have been It is used in places such as buildings, kitchens, offices and hospitals. For example, exterior wall tiles coated with titanium dioxide can give buildings self-cleaning and air-purifying properties. However, titanium dioxide photocatalytic c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/85B01J21/06C01G23/053
Inventor 付贤智陈木高刘平戴文新陈栩李朝晖陈旬王绪绪郑华荣
Owner FUZHOU UNIVERSITY