A production method and technology of activated carbon, which is applied in the technical field of art painting, decorative art, decorative structure, etc., can solve the problems of airtightness of the carbon plate, affect the adsorption and purification of harmful gases by activated carbon, and have not been developed, so as to achieve fast adsorption speed , Rich patterns and colors, long-term use effect

Inactive Publication Date: 2009-12-02
王立新
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, most domestic formed activated carbon products only use the adsorption function of activated carbon, and have not developed other functions. The carbon plates of some formed activated carbon products are not breathable, which directly affects the ability of activated carbon to absorb and purify harmful gases.
In addition, most of the decorative handicrafts sold on the market use glue that is harmful to the human body for bonding, containing harmful substances such as benzene, xylene, and formaldehyde, which can easily induce various chronic diseases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing active carbon slab and carbon slab painting
  • Method for manufacturing active carbon slab and carbon slab painting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Embodiment 1, a kind of preparation method of activated carbon charcoal plate, comprises the following steps:

[0036] 1) by weight percentage, add 2% binding agent in 98% gac;

[0037] 2) The activated carbon material obtained in step 1 is injected into the carbon plate mold, and a hydraulic press is used to apply 40 tons of pressure, and after 5 minutes of stagnation, the mold is ejected and formed;

[0038] 3) Put the prepared charcoal into the drying box, and gradually raise the temperature to 120°C for 10 hours.

[0039] The activated carbon described in the method is fruit shell activated carbon. The adhesive is an environmentally friendly corn adhesive. The size of the activated carbon is 30 mesh.

Embodiment 2

[0040] Embodiment 2, a kind of preparation method of activated carbon charcoal plate, comprises the following steps:

[0041] 1) by weight percentage, add 5% binding agent in 95% activated carbon;

[0042] 2) The activated carbon material obtained in step 1 is injected into the carbon plate mold, and a hydraulic press is used to apply 40 tons of pressure, and after 3 minutes of stagnation, the mold is ejected and formed;

[0043] 3) Put the prepared charcoal into the drying box, and gradually raise the temperature to 130°C for 15 hours.

[0044] The activated carbon described in the method is wood powder charcoal. The adhesive is an environmentally friendly corn adhesive. The size of the activated carbon is 60 mesh.

Embodiment 3

[0045] Embodiment 3, a kind of preparation method of activated carbon charcoal plate, comprises the following steps:

[0046] 4) by weight percentage, add 10% binding agent in 90% activated carbon;

[0047] 5) The activated carbon material obtained in step 1 is injected into the carbon plate mould, and a hydraulic press is used to apply 30 tons of pressure, and after stagnation for 1 minute, the mold is ejected and formed;

[0048] 6) Put the prepared charcoal into the drying box, and gradually raise the temperature to 150°C for 20 hours.

[0049] The activated carbon described in the method is coal-based powdered carbon. The adhesive is an environmentally friendly corn adhesive. The size of the activated carbon is 100 mesh.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for manufacturing a decoration material and a decoration, in particular to a method for manufacturing an active carbon slab. The method comprises the following steps: firstly, adding a bonding agent in active carbon; then, injecting the active carbon material in a carbon slab die to carry out shaping and pattern drawing; and finally, putting the material in a drying cabinet. The invention also provides a method for manufacturing active carbon slab paintings, and the method comprises the steps of pruning, polishing, decorating, embroidering, and the like. The carbon slab and the decoration thereof made by the method have simple process, aesthetic appearance and excellent air purification function.

Description

technical field [0001] The invention relates to a method for making a decoration material and a method for making an ornament. Background technique [0002] At present, the most common block paintings are cloisonné and wood block paintings. Cloisonne block paintings are made by painting patterns on the surface of copper ware with various enamel, with copper or gold and silver wires embedded around the pattern, and then calcined at high fire. The process is complicated; the wooden board painting is carved with relief patterns on the wooden board, and the colored particles are pasted on the relief patterns, but the wood is not wear-resistant, easy to tarnish, easy to be eaten by insects, easy to deform, difficult to maintain, high maintenance cost, and waste of resources. [0003] Due to the progress of society, the development of science and technology, and the improvement of people's living standards, some new furniture and decorative materials have entered people's offices ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B44D2/00B44C3/04
Inventor 王立新
Owner 王立新
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap