Al-Mg-Mn-Zr-Sr alloy and preparation method thereof

Abstract

The invention relates to a medium- and high-strength, high-toughness and weldable Al-Mg-Mn-Zr-Sr alloy containing strontium, which consists of the components of Al, MG, Mn, Zr and Sr. A preparation method thereof comprises the following steps: preparing raw materials according to the weight percentage of each component; then heating the components to 820 DEG C to 850 DEG C, totally melting, reducing temperature, standing, refining with C2Cl6, pouring into a preheat mould; after homogenizing cast ingot, heating, and extruding to deform with the extruding ratio of 12. The invention is reasonablein component proportion, easy to process and manufacture, simple in operation process and uses Sr element for alloying, thereby effectively improving the organizational structure of aluminum alloy, the comprehensive mechanical property of aluminum alloy and is adapted for industrialized application. The invention provides an achievable way to improve the comprehensive mechanical property of the medium- and high-strength and weldable aluminum alloy in the Al-Mg-Mn-Zr-Sr system.

Description

technical field [0001] The invention discloses a medium-high-strength and high-toughness weldable Al-Mg-Mn-Zr-Sr alloy and a preparation method thereof, belonging to the field of high-performance structural materials. Background technique [0002] Al-Mg series alloys are heat-treated non-strengthenable aluminum alloys, which can be used after cold working and stabilized annealing. This alloy has medium strength, good corrosion resistance and weldability. It is used in aviation, aerospace, chemical industry, electronics, automobiles and machinery. Widely used in manufacturing. However, with the development of aviation, aerospace, and ship technology, the strength of aluminum-magnesium alloys needs to be further improved. [0003] Since the heat treatment of this alloy metal cannot strengthen the alloy, appropriate microalloying treatment is adopted to obtain finer grains to play a role of fine grain strengthening, and at the same time, the submicron particles formed during t...

AI Technical Summary

Problems solved by technology

[0004] As a cheap alkaline earth element, strontium element has simple preparation process and low price in the middle of Al-Sr, but it has not been widely used in aluminum alloys. It is only used as a part of Al-Si casting alloys. In the field of wrought aluminum alloys, it is only found that it has been used as a trace element in the 6069 aluminum alloy registered in the United States in 1994, but it has not yet been used to improve Al-Mg-Mn by alloying technology of strontium. - Literature report on the mechanical properties of high-strength weldable aluminum alloys in the Zr series

Images