Coal mine underground rubber hose for drawing out methane and preparation method thereof
A rubber hose, coal mine technology, used in hoses, gas discharge, mining equipment, etc., can solve the problems of high volume resistivity, accidents, and difficulty in exporting static charges.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0043] The main material nitrile rubber was purchased from Gansu Lanhua Company, neoprene 121 was purchased from Chongqing Changshou Chemical Co., Ltd., and acetylene carbon black was purchased from Jiaozuo Hexing Chemical Industry Co., Ltd.
[0044] Take 180Kg of natural rubber, 120Kg of neoprene rubber, 150Kg of nitrile rubber, 150Kg of acetylene carbon black, 45Kg of carbon black N375, 45Kg of phthalic acid, 54Kg of dibutyl phthalate, 54Kg of antimony trioxide, and decabromopropyl ether 21kg, aluminum hydroxide 150Kg, paraffin 24Kg.
[0045] 1) Baking rubber: Baking temperature is 50-60°C for natural rubber, 50-60°C for nitrile rubber, 40-50°C for neoprene, and the drying time is 24 hours.
[0046] 2) Cut the rubber: take the raw rubber out of the drying room, wash off the surface glue, sand and impurities with a brush, and cut it into small pieces of 5-10Kg.
[0047] 3) Glue breaking: 16-inch rubber mixing machine, the roller temperature is controlled at about 45-55°C, th...
Embodiment 2
[0057] Take 180Kg of natural rubber, 90Kg of neoprene rubber, 120Kg of nitrile rubber, 120Kg of acetylene carbon black, 45Kg of carbon black N375, 60Kg of phthalic acid, 30Kg of dibutyl phthalate, 45Kg of antimony trioxide, and decabromopropyl ether 15kg, aluminum hydroxide 120Kg, paraffin 45Kg.
[0058] The preparation method is the same as in Example 1.
Embodiment 3
[0060] Take 165Kg of natural rubber, 135Kg of neoprene, 105Kg of nitrile rubber, 150Kg of conductive furnace black, 24Kg of carbon black N375, 30Kg of phthalic acid, 60Kg of dibutyl phthalate, 60Kg of antimony trioxide, and decabromopropyl ether 21kg, aluminum hydroxide 150Kg, paraffin 24Kg.
[0061] The preparation method is the same as in Example 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com